表面处理技术在模具发展中有着重要的作用。这是我为大家整理的表面处理技术论文，仅供参考!
显示器防护玻璃表面处理技术
摘 要：采用酸溶液湿法腐蚀和镀制增透、保护膜层的方法，对某型仪表用显示器防护玻璃表面进行了工艺处理，使得表面反射率降低到2%以下，产品可见光波段平均透过率达到86%，表面硬度提高到7.0GPa。产品性能检测和试用情况表明，防护玻璃具有较好的防眩、增透和抗划伤的作用，使用效果良好。
关键词： 防护玻璃;表面处理;反射率;硬度
中图分类号：TQ34 文献标识码：A
Display Protective Glass Surface Treatment Technology
WANG Bao-song, ZHANG Guo-sheng, XIE Qin
(Jinling machine factory of Jiangsu province, Nanjing Jiangsu 211100, China)
Abstract: Display protective glasses of a certain type instrument were technically processed by use of wet etching with acid solution and AR protective coating method. The reflectivity of surface was reduced to 2% below, the average transmittance of products was 86% in visible light, and the hardness of surface was enhanced to 7.0 GPa. The products' performance testing and trials expressed that, the protective glasses have good anti-glare, antireflective, scratch-resistant process and good behaviors.
Keywords: protective glasses; surface treatment; reflectivity; hardness
引 言
显示器作为当今社会一种极为常见的数据和信息的显示方式，在电脑、手机、仪器、仪表等多种设备上具有广泛的应用。根据特殊使用环境的要求，一些仪器设备的显示器往往不直接暴露于外界环境之下，而是在其外部增加一层防护玻璃。防护玻璃的作用主要是保护显示器，防止损坏。针对室外使用情况而言，由于外界视场中光源的强光会在玻璃表面形成较强的反射，影响显示图像在人眼的视觉效果，因此保护玻璃需要具有防眩光、增加透射的作用。王承遇等对玻璃表面结构、表征、测试和处理等方面技术的发展情况进行了报道[1]，文献[2]中指出防眩有三种途径：表面刻蚀、喷涂小颗粒成膜和表面镀膜。在多种防眩处理方法中，化学蚀刻因其方法简单、操作容易、适合于大面积玻璃蚀刻和大规模生产特点而倍受关注[3]。
本文介绍了对某型仪表用显示器防护玻璃的表面工艺处理的工作情况，采取酸溶液化学腐蚀的方法对防护玻璃表面进行处理以增加表面粗糙度，通过条件调节控制表面光泽度指标，使产品达到防眩作用亦不影响人眼视觉效果。后续采用硬质膜料在产品表面制备光学增透膜层，提高产品在可见光波段的透射率和表面硬度。本文制备的防护玻璃具有防眩、增透、抗划伤的作用，达到了较好的使用效果。
1 防眩层的制备
1.1 工艺条件
经材料成分分析，防护玻璃基材是以SiO2为主体，包含Na、Ca、Mg、K等离子的非晶氧化物。文献[4]中报道了在玻璃表面上采用化学腐蚀方法制备折射率连续变化的非均匀膜，该薄膜是折射率渐变的多微孔性结构，在宽光谱范围内有低的反射率，是一种耐久力较好的减反射膜。罗春炼等通过溶液组分含量的调整，研究了提高防眩玻璃透光率的影响因素[5]。对于制备条件上的控制而言，则需要适宜的腐蚀处理条件(温度、时间、反应物成分等因素)，才能使玻璃获得较高的透过率和雾度指标，以达到较好的防眩效果[2]。黄腾超等进行了应用于MOEMS器件的K9玻璃湿法刻蚀工艺的研究[6]。
本文对玻璃所进行的湿法刻蚀，是采用氢氟酸和硝酸为腐蚀液，通过调节酸液比例、温度和时间参数，达到最佳腐蚀效果。腐蚀溶液是以1:1:2比例配比的氢氟酸、硝酸和水混合溶液，腐蚀温度为40℃，刻蚀时间为18～20min。刻蚀效果的评价指标为表面光泽度，即代表了表面反射率的指标高低。本文经试验制得的表面光泽度为50～51的保护玻璃，其性能符合产品性能要求的表面反射率小于2%的技术指标，达到对产品预定的刻蚀效果。
1.2 制备过程
按1:1:2的比例配比氢氟酸、硝酸和水的混合溶液，置于聚四氟乙烯容器瓶内。用水洗方法清洗玻璃表面，不需要腐蚀处理的一面用胶带纸屏蔽起来，将玻璃样片浸泡于混合液中，整体置于水浴恒温箱内，设置水浴恒温箱温度至40℃，保持时间18～20min。反应结束后立即取出玻璃样片，用蒸馏水清洗表面残留混合液，去除屏蔽层，并烘干表面水分。采用表面光学测定仪测量玻璃处理表面的光学反射特性，以保证样品质量。
2 增透、保护膜层的制备
2.1 膜层设计
根据防护玻璃产品的特点要求，需要在表面制备增透、保护膜层以增加光学透射和提高表面硬度。根据双层减反射膜设计原理，若限定镀制在折射率为ng的基底材料上的外层折射率为n1、内层折射率为n2的两层膜的厚度都是λ/4时，欲使波长λ0的反射光减至零，它们的折射率满足如下关系[4]
基底玻璃材料的折射率为1.517，若外层膜选用折射率为1.38的MgF2膜料，经(1)式计算可得n2值为1.70，故内层选用折射率为1.66的Al2O3膜料。在双层减反射膜的基础上构建三层减反射膜，在此两层膜中间插入半波长的ZrO2层，使得透射光谱平滑。在此基础上，对三层膜系结构进行优化，将厚度做了细微调节，使得平均透光率进一步提高，最后膜系结构为G/0.083Al2O3 0.125ZrO2 0.095MgF2/Air。膜系结构中采用了硬度较高Al2O3膜料，有助于提高防护玻璃表面硬度。
2.2 制备方法
文中所采用的镀膜设备为北京科学仪器有限公司生产的zzs-1100型光学真空镀膜机，有分子泵、行星转动装置、清洗离子源、光学膜厚监控仪的电子枪加热蒸发镀膜设备。镀膜前对防护玻璃表面使用乙醚溶液擦拭干净，进腔后进行离子清洗以改善表面性质，后按照膜系结构进行薄膜制备。工艺参数如表1所示。
2.3 指标检测
对膜层的光谱、附着力、摩擦等环境适应性进行了测试，膜层光谱测试曲线如图1所示，膜层的在0.4～0.76μm可见光波段范围内的平均透过率达到99%以上。经试验检测，膜层可通过GJB 2485-1995光学膜层通用规范[7] 对附着力、摩擦、温度、湿热、清擦性、耐溶性和水溶性的检测项目，质量可靠。
3 表面处理效果评析
经过防眩层处理和薄膜镀制的防护玻璃样件制作完成后，对其进行了性能指标检测。通过UV-3600紫外、可见、近红外分光光度计对样件可见光波段光谱进行测试，透射光谱曲线如图2所示，平均透光率达到86%。采用显微硬度计对玻璃样片进行硬度测试，镀膜后表面硬度达到7.0GPa，高于玻璃基底的表面硬度6.6GPa，提高了玻璃表面硬度和抗划伤能力。将防护玻璃安装于仪表显示器上，对其实际使用效果进行测试。在显示器通电状态下，通过人眼观察，显示器表面呈现清晰的图像画面。在太阳光照射情况下观察，显示器图像画面依然清晰，反射太阳光较弱，对人眼没有造成图像不清晰或不适的感觉，整体使用效果良好。
4 结 论
本文对某型仪表用显示器防护玻璃表面进行工艺处理，采用酸溶液湿法腐蚀处理获得防眩层，后利用电子枪加热蒸发镀膜方法制备表面增透、保护膜层。防护玻璃经湿法腐蚀处理，表面反射率指标降低到2%以下，镀制增透、保护膜层后，在可见光波段的平均透过率达到86%，表面硬度提高到7.0GPa。通过性能指标、环境试验和产品试用的方法对产品工艺处理效果进行评析，结果表明，采用该工艺处理的防护玻璃具有较好的防眩、增透和抗划伤的作用，使用效果良好。
参考文献
[1] 王承遇，潘玉昆，卢 琪等. 玻璃表面工程的进展[J]. 玻璃与搪瓷，2003，31(5)：45-50.
[2] 吴春春，杨 辉，袁 骏等. 抗静电防眩膜研究进展[J]. 材料科学与工程，2002，20(1)：133-135.
[3] 胡沛然，韩文爵，王海风等. Na2SiF6和ZnCl2对玻璃防眩光效果的影响研究[J]. 化工新型材料，2009，37(11)：84-95.
[4] 唐晋发，顾培夫，刘 旭等. 现代光学薄膜技术[M]. 杭州：浙江大学出版社，2006.
[5] 罗春炼，韩文爵，王海风等. 提高防眩玻璃透过率的主要影响因素[J]. 化工新型材料，2008，36(12)：89-91.
[6] 黄腾超，沈亦兵，陈海星等. 应用于MOEM S器件的K9玻璃湿法刻蚀工艺的研究[J]. 光学仪器，2004，26(2)：151-155.
[7] 国防科学技术委员会. 中华人民共和国军用标准 光学膜层通用规范 GJB 2485-1995[B]. 中国标准出版社，1995.省略。
铝合金燃油箱表面处理技术
【摘 要】本文概述了铝合金的表面处理技术，通过试验验证了几种铝合金的表面处理技术，分析了铝合金燃油箱的表面处理可行性，对解决铝合金燃油箱表面氧化变暗问题，提升产品外观，延长油箱寿命等具有积极意义。
【关键词】铝合金;燃油箱;钝化;氧化;金属覆膜剂
前言
随着重卡轻量化的发展重卡上的铁质燃油箱逐渐被铝质燃油箱替代，燃油箱采用铝合金材料，不但自重减轻一半以上，内部不生锈，而且铝合金燃油箱以光洁的表面深受用户的青睐，因此这种燃油箱市场前景广阔，逐渐成为应用趋势。但是铝合金燃油箱顾客购买时外观鲜亮，色泽美观，使用大约1年左右铝合金燃油箱“黯然失色”，其表面被雨水、泥沙等腐蚀后，色泽发暗，局部产生白色粉状霉点、发黄，油箱整体色泽不一，严重影响顾客的满意度，见下图1，通过对国内规模化油箱生产企业的了解，发现铝合金燃油箱的表面腐蚀，变色各油箱生产企业都遇到过，各生产企业也在一直寻求铝油箱的表面处理技术，鉴于此笔者对铝合金燃油箱的表面处理技术进行了研究。
图1 腐蚀后的油箱
1 铝制品表面处理技术概述
铝合金燃油箱材料为铝镁合金5052，属于防锈铝，其表面自然形成一层极薄的氧化膜(0.01-0.02um)，有一定的抗腐蚀能力。但这层氧化膜疏松多孔，不均匀，抗腐蚀能力不强，容易沾染污迹，因此铝合金制品通常要进行特殊的表面处理，铝合金的表面处理技术有：钝化、阳极氧化、电镀、喷涂等，这几种处理技术都比较成熟，在一些铝制品上均有应用。
电镀处理技术：铝合金燃油箱是封闭的空心容器，其重量轻，体积大，电镀虽然是一种成熟的处理工艺，电镀层外观漂亮、其耐腐蚀性也较好，但是在铝合金上直接电镀是相当困难的，因为铝表面的氧化膜使得电镀层对铝的附着力很差，因此铝合金电镀必须有特殊的表面预处理，再者铝合金的电镀成本较高，使得这种处理方式并不适合应用于铝合金燃油箱上。
喷涂处理技术：该技术的关键在于解决涂层与铝基体的附着力，因此喷涂前铝合金表面必须进行预处理，其表面预处理需要喷砂或拉毛，再加上磷化或钝化、氧化等形成喷涂底层后，才能形成良好漆膜。其工艺流程较多，喷漆成本较高，其漆膜颜色缺乏金属质感，一般顾客青睐铝合金金属的本色，因此这种处理技术也不适合铝合金燃油箱。若顾客对铝合金燃油箱的外观颜色有特殊要求，比如我公司根据客户的特殊要求也生产黑色的铝合金燃油箱，这种铝合金燃油箱必须经过预处理才能进行粉末喷涂，喷涂后的燃油箱经检测其外表面的耐腐蚀、耐侯性等性能都非常优良，只是产品成本较高。
阳极氧化、钝化、金属覆膜剂等处理技术：铝合金的表面处理技术中阳极氧化是应用最光与最成功的技术，也是研究和开发最深入与最全面的技术，经过阳极氧化处理其表面生成的氧化膜，耐蚀性、耐磨性、装饰性都有显著的提升，其表面可以生成透明的膜，也可以着色成各种彩色的膜。铝合金的钝化处理、金属覆膜剂处理等其工艺流程简单可以将铝制品直接浸入钝化液或者金属覆膜剂溶液中，也可以喷淋在铝制品上。这种处理技术属于化学转化处理，其表面形成的化学转化膜整体性能虽不及阳极氧化膜，但是这种处理技术经济、简便、快速、生产线简单，特别适合大批量零部件的低成本生产。
每种铝制品需要考虑多种因素，选择适合具体产品的处理技术，铝合金燃油箱的表面处理技术方面，目前国内对其研究的还较少，还没有成熟的处理工艺。为此笔者根据铝合金燃油箱的特点，对几种有可能应用的处理技术开展了工艺试验，探索最适合铝合金燃油箱的表面处理技术。
2 铝板表面处理技术试验过程
2.1 提供的试板情况
(1)阳极氧化膜试验，分别对铝合金板材进行了5um ，8um，12um的阳极氧化试验;
(2)透明钝化膜试验，与某钝化技术公司合作开展了铝合金的透明钝化处理试验;
(3)覆膜剂试验，与某化工公司合作开发的铝合金用金属覆膜剂，开展了相关工艺试验。
2.2 开展的试验如下
(1)耐柴油性试验
经各种表面处理的铝板，浸入柴油，经过120h浸泡，检验铝板表面膜层的完好性、附着力、厚度等都合格。
(2)耐泥浆试验
对各种表面处理的铝板经过240小时耐泥浆试验，试验结果全部合格，
(3)盐雾试验
进行了96h的盐雾试验，经处理的试板全部合格，随后再经过120h的盐雾试验，经处理的试板全部合格。
(4)耐灰浆(水泥)试验
第一次试验96h，第二次试验120h，试板经第一次96h水泥试验，未进行表面处理铝板不合格，其余铝板全部合格，第二次经120h水泥试验，透明钝化及金属覆膜处理的铝板合格，阳极氧化处理铝板有轻微腐蚀痕迹，清洗后留有白色痕迹。
2.3 试验结果分析
针对铝合金燃油箱的特殊性，笔者对成熟的几种铝板表面处理技术开展了相关工艺试验，对每种表面处理的铝板都进行了耐柴油性试验，耐泥浆试验，盐雾试验，耐水泥试验。从试验结果来看透明钝化表面处理技术，在铝板表面形成的钝化膜抵抗外界各种腐蚀的的能力较强，能够满足铝合金燃油箱的使用要求;阳极氧化表面处理技术，在铝板表面形成的阳极氧化膜，在耐水泥试验后表面存在轻微的腐蚀，通过对这种阳极氧化膜的深入分析，阳极氧化膜的膜厚及封孔质量是关键控制点，通过对本试验形成的阳极氧化膜检测，其封孔质量不达标，这种阳极氧化膜的其他性能满足使用要求，通过对5um、8um、12um阳极氧化膜的分析，考虑成本及阳极氧化膜的色泽与铝合金燃油箱的本色差别，5um、8um的阳极氧化膜可以应用于铝合金燃油箱的表面处理，需要注意控制阳极氧化膜的封孔质量。
表面进行金属覆膜剂处理，这种表面处理技术与透明钝化的处理技术类似，其优良的耐油、耐高温、防腐及操作方便性，在不改变金属现有外观情况下对各类易氧化金属表面可轻松实现长效防腐效果，是这几种处理技术效果最优的处理方式。
3 结论
本文针对铝合金燃油箱的使用要求开展了相关试验，通过试验验证了透明钝化、阳极氧化、金属覆膜剂表面处理技术应用于铝合金燃油箱的可行性。通过对铝合金燃油箱的适当的表面处理，不仅提高了铝产品外观，还改进了耐蚀、耐候性，满足了铝合金燃油箱的特殊使用要求，延长了产品使用寿命。
本文介绍的透明钝化、阳极氧化、金属覆膜剂表面处理技术，效果好，成本低，可以应用于铝合金燃油箱的工业化生产。
参考文献：
[1]朱祖芳.铝合金阳极氧化与表面处理技术[M].北京：化学工业出版社，2004.
铝合金:一。用途铝合金是纯铝加入一些合金元素制成的，如铝—锰合金、铝—铜合金、铝—铜—镁系硬铝合金、铝—锌—镁—铜系超硬铝合金。铝合金比纯铝具有更好的物理力学性能：易加工、耐久性高、适用范围广、装饰效果好、花色丰富。铝合金分为防锈铝、硬铝、超硬铝等种类，各种类均有各自的使用范围，并有各自的代号，以供使用者选用。 铝合金仍然保持了质轻的特点，但机械性能明显提高。铝合金材料的应用有以下三个方面：一是作为受力构件；二是作为门、窗、管、盖、壳等材料；三是作为装饰和绝热材料。利用铝合金阳极氧化处理后可以进行着色的特点，制成各种装饰品。铝合金板材、型材表面可以进行防腐、轧花、涂装、印刷等二次加工，制成各种装饰板材、型材，作为装饰材料。 铝合金是应用最广的一种防锈铝，它的强度不高，不能热处理强化，在退火状态下有高的塑性，而蚀性好，焊接性好，切削加工性不良。用於制造要求高可塑性和良好焊接性、在液体或气体介质中工作的低载荷零件如油箱、油管、液体容器等；线材可制作铆钉。 二。铝合金概述（资料）以铝为基的合金总称。主要合金元素有铜、硅、镁、锌、锰，次要合金元素有镍、铁、钛、铬、锂等。 铝合金密度低，但强度比较高，接近或超过优质钢，塑性好，可加工成各种型材，具有优良的导电性、导热性和抗蚀性，工业上广泛使用，使用量仅次于钢。 铝合金分两大类：铸造铝合金，在铸态下使用；变形铝合金，能承受压力加工，力学性能高于铸态。可加工成各种形态、规格的铝合金材。主要用于制造航空器材、日常生活用品、建筑用门窗等。 铝合金按加工方法可以分为变形铝合金和铸造铝合金。变形铝合金又分为不可热处理强化型铝合金和可热处理强化型铝合金。不可热处理强化型不能通过热处理来提高机械性能，只能通过冷加工变形来实现强化，它主要包括高纯铝、工业高纯铝、工业纯铝以及防锈铝等。可热处理强化型铝合金可以通过淬火和时效等热处理手段来提高机械性能，它可分为硬铝、锻铝、超硬铝和特殊铝合金等。 铝合金可以采用热处理获得良好的机械性能，物理性能和抗腐蚀性能。 铸造铝合金按化学成分可分为铝硅合金，铝铜合金，铝镁合金和铝锌合金。[编辑本段]【纯铝产品】 纯铝分冶炼品和压力加工品两类，前者以化学成份Al表示，后者用汉语拼音LG（铝、工业用的）表示。[编辑本段]【压力加工铝合金】 铝合金压力加工产品分为防锈（LF）、硬质（LY）、锻造（LD）、超硬（LC）、包覆（LB）、特殊（LT）及钎焊（LQ）等七类。常用铝合金材料的状态为退火（M焖火）、硬化（Y）、热轧（R）等三种。[编辑本段]【铝材】 铝和铝合金经加工成一定形状的材料统称铝材，包括板材、带材、箔材、管材、棒材、线材、型材等。[编辑本段]【铸造铝合金】 铸造铝合金（ZL）按成分中铝以外的主要元素硅、铜、镁、锌分为四类，代号编码分别为100、200、300、400。[编辑本段]【高强度铝合金】 高强度铝合金指其抗拉强度大于480兆帕的铝合金，主要是压力加工铝合金中硬铝合金类、超硬铝合金类和铸造合金类。[编辑本段]【铝合金缺陷修复】 铝合金在生产过程中，容易出现缩孔、砂眼、气孔和夹渣等铸造缺陷。如何修复铝合金铸件气孔等缺陷呢？如果用电焊、氩焊等设备来修补，由于放热量大，容易产生热变形等副作用，无法满足补焊要求。 冷焊修复机是利用高频电火花瞬间放电、无热堆焊原理来修复铸件缺陷。由于冷焊热影响区域小，不会造成基材退火变形，不产生裂纹、没有硬点、硬化现象。而且熔接强度高，补材与基体同时熔化后的再凝固，结合牢固，可进行磨、铣、锉等加工，致密不脱落。冷焊修复机是修补铝合金气孔、砂眼等细小缺陷的理想方法。[编辑本段]【不同牌号铝合金的典型用途】 合 金 典 型 用 途 1050 食品、化学和酿造工业用挤压盘管，各种软管，烟花粉 1060 要求抗蚀性与成形性均高的场合，但对强度要求不高，化工设备是其典型用途 1100 用于加工需要有良好的成形性和高的抗蚀性但不要求有高强度的零件部件，例如化工产品、食品工业装置与贮存容器、薄板加工件、深拉或旋压凹形器皿、焊接零部件、热交换器、印刷板、铭牌、反光器具 1145 包装及绝热铝箔，热交换器 1199 电解电容器箔，光学反光沉积膜 1350 电线、导电绞线、汇流排、变压器带材 2011 螺钉及要求有良好切削性能的机械加工产品 2014 应用于要求高强度与硬度（包括高温）的场合。飞机重型、锻件、厚板和挤压材料，车轮与结构元件，多级火箭第一级燃料槽与航天器零件，卡车构架与悬挂系统零件 2017 是第一个获得工业应用的2XXX系合金，目前的应用范围较窄，主要为铆钉、通用机械零件、结构与运输工具结构件，螺旋桨与配件 2024 飞机结构、铆钉、导弹构件、卡车轮毂、螺旋桨元件及其他种种结构件 2036 汽车车身钣金件 2048 航空航天器结构件与兵器结构零件 2124 航空航天器结构件 2218 飞机发动机和柴油发动机活塞，飞机发动机汽缸头，喷气发动机叶轮和压缩机环 2219 航天火箭焊接氧化剂槽，超音速飞机蒙皮与结构零件，工作温度为-270~300摄氏度。焊接性好，断裂韧性高，T8状态有很高的抗应力腐蚀开裂能力 2319 焊拉2219合金的焊条和填充焊料 2618 模锻件与自由锻件。活塞和航空发动机零件 2A01 工作温度小于等于100摄氏度的结构铆钉 2A02 工作温度200~300摄氏度的涡轮喷气发动机的轴向压气机叶片 2A06 工作温度150~250摄氏度的飞机结构及工作温度125~250摄氏度的航空器结构铆钉 2A10 强度比2A01合金的高，用于制造工作温度小于等于100摄氏度的航空器结构铆钉 2A11 飞机的中等强度的结构件、螺旋桨叶片、交通运输工具与建筑结构件。航空器的中等强度的螺栓与铆钉 2A12 航空器蒙皮、隔框、翼肋、翼梁、铆钉等，建筑与交通运输工具结构件 2A14 形状复杂的自由锻件与模锻件 2A16 工作温度250~300摄氏度的航天航空器零件，在室温及高温下工作的焊接容器与气密座舱 2A17 工作温度225~250摄氏底的航空器零件 2A50 形状复杂的中等强度零件 2A60 航空器发动机压气机轮、导风轮、风扇、叶轮等 2A70 飞机蒙皮，航空器发动机活塞、导风轮、轮盘等 2A80 航空发动机压气机叶片、叶轮、活塞、涨圈及其他工作温度高的零件 2A90 航空发动机活塞 3003 用于加工需要有良好的成形性能、高的抗蚀性可焊性好的零件部件，或既要求有这些性能又需要有比1XXX系合金强度高的工作，如厨具、食物和化工产品处理与贮存装置，运输液体产品的槽、罐，以薄板加工的各种压力容器与管道 3004 全铝易拉罐罐身，要求有比3003合金更高强度的零部件，化工产品生产与贮存装置，薄板加工件，建筑加工件，建筑工具，各种灯具零部件 3105 房间隔断、档板、活动房板、檐槽和落水管，薄板成形加工件，瓶盖、瓶塞等 3A21 飞机油箱、油路导管、铆钉线材等；建筑材料与食品等工业装备等 5005 与3003合金相似，具有中等强度与良好的抗蚀性。用作导体、炊具、仪表板、壳与建筑装饰件。阳极氧化膜比3003合金上的氧化膜更加明亮，并与6063合金的色调协调一致 5050 薄板可作为致冷机与冰箱的内衬板，汽车气管、油管与农业灌溉管；也可加工厚板、管材、棒材、异形材和线材等 5052 此合金有良好的成形加工性能、抗蚀性、可烛性、疲劳强度与中等的静态强度，用于制造飞机油箱、油管，以及交通车辆、船舶的钣金件，仪表、街灯支架与铆钉、五金制品等 5056 镁合金与电缆护套铆钉、拉链、钉子等；包铝的线材广泛用于加工农业捕虫器罩，以及需要有高抗蚀性的其他场合 5083 用于需要有高的抗蚀性、良好的可焊性和中等强度的场合，诸如舰艇、汽车和飞机板焊接件；需严格防火的压力容器、致冷装置、电视塔、钻探设备、交通运输设备、导弹元件、装甲等 5086 用于需要有高的抗蚀性、良好的可焊性和中等强度的场合，例如舰艇、汽车、飞机、低温设备、电视塔、钻井装置、运输设备、导弹零部件与甲板等 5154 焊接结构、贮槽、压力容器、船舶结构与海上设施、运输槽罐 5182 薄板用于加工易拉罐盖，汽车车身板、操纵盘、加强件、托架等零部件 5252 用于制造有较高强度的装饰件，如汽车等的装饰性零部件。在阳极氧化后具有光亮透明的氧化膜 5254 过氧化氢及其他化工产品容器 5356 焊接镁含量大于3%的铝-镁合金焊条及焊丝 5454 焊接结构，压力容器，海洋设施管道 5456 装甲板、高强度焊接结构、贮槽、压力容器、船舶材料 5457 经抛光与阳极氧化处理的汽车及其他装备的装饰件 5652 过氧化氢及其他化工产品贮存容器 5657 经抛光与阳极氧化处理的汽车及其他装备的装饰件，但在任何情况下必须确保材料具有细的晶粒组织 5A02 飞机油箱与导管，焊丝，铆钉，船舶结构件 5A03 中等强度焊接结构，冷冲压零件，焊接容器，焊丝，可用来代替5A02合金 5A05 焊接结构件，飞机蒙皮骨架 5A06 焊接结构，冷模锻零件，焊拉容器受力零件，飞机蒙皮骨部件 5A12 焊接结构件，防弹甲板 6005 挤压型材与管材，用于要求强高大于6063合金的结构件，如梯子、电视天线等 6009 汽车车身板 6010 薄板：汽车车身 6061 要求有一定强度、可焊性与抗蚀性高的各种工业结构性，如制造卡车、塔式建筑、船舶、电车、家具、机械零件、精密加工等用的管、棒、形材、板材 6063 建筑型材，灌溉管材以及供车辆、台架、家具、栏栅等用的挤压材料 6066 锻件及焊接结构挤压材料 6070 重载焊接结构与汽车工业用的挤压材料与管材 6101 公共汽车用高强度棒材、电导体与散热器材等 6151 用于模锻曲轴零件、机器零件与生产轧制环，供既要求有良好的可锻性能、高的强度，又要有良好抗蚀性之用 6201 高强度导电棒材与线材 6205 厚板、踏板与耐高冲击的挤压件 6262 要求抗蚀性优于2011和2017合金的有螺纹的高应力零件 6351 车辆的挤压结构件，水、石油等的输送管道 6463 建筑与各种器具型材，以及经阳极氧化处理后有明亮表面的汽车装饰件 6A02 飞机发动机零件，形状复杂的锻件与模锻件 7005 挤压材料，用于制造既要有高的强度又要有高的断裂韧性的焊接结构，如交通运输车辆的桁架、杆件、容器；大型热交换器，以及焊接后不能进行固熔处理的部件；还可用于制造体育器材如网球拍与垒球棒 7039 冷冻容器、低温器械与贮存箱，消防压力器材，军用器材、装甲板、导弹装置 7049 用于锻造静态强度与7079-T6合金的相同而又要求有高的抗应力腐蚀开裂勇力的零件，如飞机与导弹零件——起落架液压缸和挤压件。零件的疲劳性能大致与7075-T6合金的相等，而韧性稍高 7050 飞机结构件用中厚板、挤压件、自由锻件与模锻件。制造这类零件对合金的要求是：抗剥落腐蚀、应力腐蚀开裂能力、断裂韧性与抗疲劳性能都高 7072 空调器铝箔与特薄带材；2219、3003、3004、5050、5052、5154、6061、7075、7475、7178合金板材与管材的包覆层 7075 用于制造飞机结构及期货 他要求强度高、抗腐蚀性能强的高应力结构件、模具制造 7175 用于锻造航空器用的高强度结构性。T736材料有良好的综合性能，即强度、抗剥落腐蚀与抗应力腐蚀开裂性能、断裂韧性、疲劳强度都高 7178 供制造航空航天器的要求抗压屈服强度高的零部件 7475 机身用的包铝的与未包铝的板材，机翼骨架、桁条等。其他既要有高的强度又要有高的断裂韧性的零部件 7A04 飞机蒙皮、螺钉、以及受力构件如大梁桁条、隔框、翼肋、起落架等[编辑本段]【变形铝及铝合金状态、代号】 1.范围 本标准规定了变形铝合金的状态代号。 本标准适用于铝及铝加工产品。 2.基本原则 2.1基础状态代号用一个英文大写字母表示。 2.2细分状态代号采用基础状态代号后跟一位或多位阿拉伯数字表示。 2.3基本状态代号 基本状态分为5种 代号 名称 说明与应用 F 自由加工状态 适用于在成型过程中，对于加工硬化和热处理条件特殊要求的产品，该状态产品的力学性能不作规定。 O 退火状态 适用于经完全退火获得最低强度的加工产品。 H 加工硬化状态 适用于通过加工硬化提高强度的产品，产品在加工硬化后可经过（也可不经过）使强度有所降低的附加热处理。 W 固熔热处理状态 处理状态 一种不稳定状态，仅适用于经固溶热处理后，室温下自然时效的合金，该状态代号仅表示产品处于自然时效阶段。 T 热处理状态(不同于F、O、H状态) 适用于热处理后，经过（或不经过）加工硬化达到稳定的产品。T代号后面必须跟有一位或多位阿拉伯数字
铝合金:一。用途铝合金是纯铝加入一些合金元素制成的，如铝—锰合金、铝—铜合金、铝—铜—镁系硬铝合金、铝—锌—镁—铜系超硬铝合金。铝合金比纯铝具有更好的物理力学性能：易加工、耐久性高、适用范围广、装饰效果好、花色丰富。铝合金分为防锈铝、硬铝、超硬铝等种类，各种类均有各自的使用范围，并有各自的代号，以供使用者选用。 铝合金仍然保持了质轻的特点，但机械性能明显提高。铝合金材料的应用有以下三个方面：一是作为受力构件；二是作为门、窗、管、盖、壳等材料；三是作为装饰和绝热材料。利用铝合金阳极氧化处理后可以进行着色的特点，制成各种装饰品。铝合金板材、型材表面可以进行防腐、轧花、涂装、印刷等二次加工，制成各种装饰板材、型材，作为装饰材料。 铝合金是应用最广的一种防锈铝，它的强度不高，不能热处理强化，在退火状态下有高的塑性，而蚀性好，焊接性好，切削加工性不良。用於制造要求高可塑性和良好焊接性、在液体或气体介质中工作的低载荷零件如油箱、油管、液体容器等；线材可制作铆钉。 二。铝合金概述（资料）以铝为基的合金总称。主要合金元素有铜、硅、镁、锌、锰，次要合金元素有镍、铁、钛、铬、锂等。 铝合金密度低，但强度比较高，接近或超过优质钢，塑性好，可加工成各种型材，具有优良的导电性、导热性和抗蚀性，工业上广泛使用，使用量仅次于钢。 铝合金分两大类：铸造铝合金，在铸态下使用；变形铝合金，能承受压力加工，力学性能高于铸态。可加工成各种形态、规格的铝合金材。主要用于制造航空器材、日常生活用品、建筑用门窗等。 铝合金按加工方法可以分为变形铝合金和铸造铝合金。变形铝合金又分为不可热处理强化型铝合金和可热处理强化型铝合金。不可热处理强化型不能通过热处理来提高机械性能，只能通过冷加工变形来实现强化，它主要包括高纯铝、工业高纯铝、工业纯铝以及防锈铝等。可热处理强化型铝合金可以通过淬火和时效等热处理手段来提高机械性能，它可分为硬铝、锻铝、超硬铝和特殊铝合金等。 铝合金可以采用热处理获得良好的机械性能，物理性能和抗腐蚀性能。 铸造铝合金按化学成分可分为铝硅合金，铝铜合金，铝镁合金和铝锌合金。[编辑本段]【纯铝产品】 纯铝分冶炼品和压力加工品两类，前者以化学成份Al表示，后者用汉语拼音LG（铝、工业用的）表示。[编辑本段]【压力加工铝合金】 铝合金压力加工产品分为防锈（LF）、硬质（LY）、锻造（LD）、超硬（LC）、包覆（LB）、特殊（LT）及钎焊（LQ）等七类。常用铝合金材料的状态为退火（M焖火）、硬化（Y）、热轧（R）等三种。[编辑本段]【铝材】 铝和铝合金经加工成一定形状的材料统称铝材，包括板材、带材、箔材、管材、棒材、线材、型材等。[编辑本段]【铸造铝合金】 铸造铝合金（ZL）按成分中铝以外的主要元素硅、铜、镁、锌分为四类，代号编码分别为100、200、300、400。[编辑本段]【高强度铝合金】 高强度铝合金指其抗拉强度大于480兆帕的铝合金，主要是压力加工铝合金中硬铝合金类、超硬铝合金类和铸造合金类。[编辑本段]【铝合金缺陷修复】 铝合金在生产过程中，容易出现缩孔、砂眼、气孔和夹渣等铸造缺陷。如何修复铝合金铸件气孔等缺陷呢？如果用电焊、氩焊等设备来修补，由于放热量大，容易产生热变形等副作用，无法满足补焊要求。 冷焊修复机是利用高频电火花瞬间放电、无热堆焊原理来修复铸件缺陷。由于冷焊热影响区域小，不会造成基材退火变形，不产生裂纹、没有硬点、硬化现象。而且熔接强度高，补材与基体同时熔化后的再凝固，结合牢固，可进行磨、铣、锉等加工，致密不脱落。冷焊修复机是修补铝合金气孔、砂眼等细小缺陷的理想方法。[编辑本段]【不同牌号铝合金的典型用途】 合 金 典 型 用 途 1050 食品、化学和酿造工业用挤压盘管，各种软管，烟花粉 1060 要求抗蚀性与成形性均高的场合，但对强度要求不高，化工设备是其典型用途 1100 用于加工需要有良好的成形性和高的抗蚀性但不要求有高强度的零件部件，例如化工产品、食品工业装置与贮存容器、薄板加工件、深拉或旋压凹形器皿、焊接零部件、热交换器、印刷板、铭牌、反光器具 1145 包装及绝热铝箔，热交换器 1199 电解电容器箔，光学反光沉积膜 1350 电线、导电绞线、汇流排、变压器带材 2011 螺钉及要求有良好切削性能的机械加工产品 2014 应用于要求高强度与硬度（包括高温）的场合。飞机重型、锻件、厚板和挤压材料，车轮与结构元件，多级火箭第一级燃料槽与航天器零件，卡车构架与悬挂系统零件 2017 是第一个获得工业应用的2XXX系合金，目前的应用范围较窄，主要为铆钉、通用机械零件、结构与运输工具结构件，螺旋桨与配件 2024 飞机结构、铆钉、导弹构件、卡车轮毂、螺旋桨元件及其他种种结构件 2036 汽车车身钣金件 2048 航空航天器结构件与兵器结构零件 2124 航空航天器结构件 2218 飞机发动机和柴油发动机活塞，飞机发动机汽缸头，喷气发动机叶轮和压缩机环 2219 航天火箭焊接氧化剂槽，超音速飞机蒙皮与结构零件，工作温度为-270~300摄氏度。焊接性好，断裂韧性高，T8状态有很高的抗应力腐蚀开裂能力 2319 焊拉2219合金的焊条和填充焊料 2618 模锻件与自由锻件。活塞和航空发动机零件 2A01 工作温度小于等于100摄氏度的结构铆钉 2A02 工作温度200~300摄氏度的涡轮喷气发动机的轴向压气机叶片 2A06 工作温度150~250摄氏度的飞机结构及工作温度125~250摄氏度的航空器结构铆钉 2A10 强度比2A01合金的高，用于制造工作温度小于等于100摄氏度的航空器结构铆钉 2A11 飞机的中等强度的结构件、螺旋桨叶片、交通运输工具与建筑结构件。航空器的中等强度的螺栓与铆钉 2A12 航空器蒙皮、隔框、翼肋、翼梁、铆钉等，建筑与交通运输工具结构件 2A14 形状复杂的自由锻件与模锻件 2A16 工作温度250~300摄氏度的航天航空器零件，在室温及高温下工作的焊接容器与气密座舱 2A17 工作温度225~250摄氏底的航空器零件 2A50 形状复杂的中等强度零件 2A60 航空器发动机压气机轮、导风轮、风扇、叶轮等 2A70 飞机蒙皮，航空器发动机活塞、导风轮、轮盘等 2A80 航空发动机压气机叶片、叶轮、活塞、涨圈及其他工作温度高的零件 2A90 航空发动机活塞 3003 用于加工需要有良好的成形性能、高的抗蚀性可焊性好的零件部件，或既要求有这些性能又需要有比1XXX系合金强度高的工作，如厨具、食物和化工产品处理与贮存装置，运输液体产品的槽、罐，以薄板加工的各种压力容器与管道 3004 全铝易拉罐罐身，要求有比3003合金更高强度的零部件，化工产品生产与贮存装置，薄板加工件，建筑加工件，建筑工具，各种灯具零部件 3105 房间隔断、档板、活动房板、檐槽和落水管，薄板成形加工件，瓶盖、瓶塞等 3A21 飞机油箱、油路导管、铆钉线材等；建筑材料与食品等工业装备等 5005 与3003合金相似，具有中等强度与良好的抗蚀性。用作导体、炊具、仪表板、壳与建筑装饰件。阳极氧化膜比3003合金上的氧化膜更加明亮，并与6063合金的色调协调一致 5050 薄板可作为致冷机与冰箱的内衬板，汽车气管、油管与农业灌溉管；也可加工厚板、管材、棒材、异形材和线材等 5052 此合金有良好的成形加工性能、抗蚀性、可烛性、疲劳强度与中等的静态强度，用于制造飞机油箱、油管，以及交通车辆、船舶的钣金件，仪表、街灯支架与铆钉、五金制品等 5056 镁合金与电缆护套铆钉、拉链、钉子等；包铝的线材广泛用于加工农业捕虫器罩，以及需要有高抗蚀性的其他场合 5083 用于需要有高的抗蚀性、良好的可焊性和中等强度的场合，诸如舰艇、汽车和飞机板焊接件；需严格防火的压力容器、致冷装置、电视塔、钻探设备、交通运输设备、导弹元件、装甲等 5086 用于需要有高的抗蚀性、良好的可焊性和中等强度的场合，例如舰艇、汽车、飞机、低温设备、电视塔、钻井装置、运输设备、导弹零部件与甲板等 5154 焊接结构、贮槽、压力容器、船舶结构与海上设施、运输槽罐 5182 薄板用于加工易拉罐盖，汽车车身板、操纵盘、加强件、托架等零部件 5252 用于制造有较高强度的装饰件，如汽车等的装饰性零部件。在阳极氧化后具有光亮透明的氧化膜 5254 过氧化氢及其他化工产品容器 5356 焊接镁含量大于3%的铝-镁合金焊条及焊丝 5454 焊接结构，压力容器，海洋设施管道 5456 装甲板、高强度焊接结构、贮槽、压力容器、船舶材料 5457 经抛光与阳极氧化处理的汽车及其他装备的装饰件 5652 过氧化氢及其他化工产品贮存容器 5657 经抛光与阳极氧化处理的汽车及其他装备的装饰件，但在任何情况下必须确保材料具有细的晶粒组织 5A02 飞机油箱与导管，焊丝，铆钉，船舶结构件 5A03 中等强度焊接结构，冷冲压零件，焊接容器，焊丝，可用来代替5A02合金 5A05 焊接结构件，飞机蒙皮骨架 5A06 焊接结构，冷模锻零件，焊拉容器受力零件，飞机蒙皮骨部件 5A12 焊接结构件，防弹甲板 6005 挤压型材与管材，用于要求强高大于6063合金的结构件，如梯子、电视天线等 6009 汽车车身板 6010 薄板：汽车车身 6061 要求有一定强度、可焊性与抗蚀性高的各种工业结构性，如制造卡车、塔式建筑、船舶、电车、家具、机械零件、精密加工等用的管、棒、形材、板材 6063 建筑型材，灌溉管材以及供车辆、台架、家具、栏栅等用的挤压材料 6066 锻件及焊接结构挤压材料 6070 重载焊接结构与汽车工业用的挤压材料与管材 6101 公共汽车用高强度棒材、电导体与散热器材等 6151 用于模锻曲轴零件、机器零件与生产轧制环，供既要求有良好的可锻性能、高的强度，又要有良好抗蚀性之用 6201 高强度导电棒材与线材 6205 厚板、踏板与耐高冲击的挤压件 6262 要求抗蚀性优于2011和2017合金的有螺纹的高应力零件 6351 车辆的挤压结构件，水、石油等的输送管道 6463 建筑与各种器具型材，以及经阳极氧化处理后有明亮表面的汽车装饰件 6A02 飞机发动机零件，形状复杂的锻件与模锻件 7005 挤压材料，用于制造既要有高的强度又要有高的断裂韧性的焊接结构，如交通运输车辆的桁架、杆件、容器；大型热交换器，以及焊接后不能进行固熔处理的部件；还可用于制造体育器材如网球拍与垒球棒 7039 冷冻容器、低温器械与贮存箱，消防压力器材，军用器材、装甲板、导弹装置 7049 用于锻造静态强度与7079-T6合金的相同而又要求有高的抗应力腐蚀开裂勇力的零件，如飞机与导弹零件——起落架液压缸和挤压件。零件的疲劳性能大致与7075-T6合金的相等，而韧性稍高 7050 飞机结构件用中厚板、挤压件、自由锻件与模锻件。制造这类零件对合金的要求是：抗剥落腐蚀、应力腐蚀开裂能力、断裂韧性与抗疲劳性能都高 7072 空调器铝箔与特薄带材；2219、3003、3004、5050、5052、5154、6061、7075、7475、7178合金板材与管材的包覆层 7075 用于制造飞机结构及期货 他要求强度高、抗腐蚀性能强的高应力结构件、模具制造 7175 用于锻造航空器用的高强度结构性。T736材料有良好的综合性能，即强度、抗剥落腐蚀与抗应力腐蚀开裂性能、断裂韧性、疲劳强度都高 7178 供制造航空航天器的要求抗压屈服强度高的零部件 7475 机身用的包铝的与未包铝的板材，机翼骨架、桁条等。其他既要有高的强度又要有高的断裂韧性的零部件 7A04 飞机蒙皮、螺钉、以及受力构件如大梁桁条、隔框、翼肋、起落架等[编辑本段]【变形铝及铝合金状态、代号】 1.范围 本标准规定了变形铝合金的状态代号。 本标准适用于铝及铝加工产品。 2.基本原则 2.1基础状态代号用一个英文大写字母表示。 2.2细分状态代号采用基础状态代号后跟一位或多位阿拉伯数字表示。 2.3基本状态代号 基本状态分为5种 代号 名称 说明与应用 F 自由加工状态 适用于在成型过程中，对于加工硬化和热处理条件特殊要求的产品，该状态产品的力学性能不作规定。 O 退火状态 适用于经完全退火获得最低强度的加工产品。 H 加工硬化状态 适用于通过加工硬化提高强度的产品，产品在加工硬化后可经过（也可不经过）使强度有所降低的附加热处理。 W 固熔热处理状态 处理状态 一种不稳定状态，仅适用于经固溶热处理后，室温下自然时效的合金，该状态代号仅表示产品处于自然时效阶段。 T 热处理状态(不同于F、O、H状态) 适用于热处理后，经过（或不经过）加工硬化达到稳定的产品。T代号后面必须跟有一位或多位阿拉伯数字
物质的用途决定于物质的性质。由于铝有多种优良性能，因而铝有着极为广泛的用途。 (1)铝的密度很小，仅为2.7 g/cm3，虽然它比较软，但可制成各种铝合金，如硬铝、超硬铝；防锈铝、铸铝等。这些铝合金广泛应用于飞机、汽车、火车、船舶等制造工业。此外，宇宙火箭、航天飞机、人造卫星也使用大量的铝及其合金。例如，一架超音速飞机约由70%的铝及其合金构成。船舶建造中也大量使用铝，一艘大型客船的用铝量常达几千吨。 (2)铝的导电性仅次于银、铜，虽然它的导电率只有铜的2/3，但密度只有铜的1/3，所以输送同量的电，铝线的质量只有铜线的一半。铝表面的氧化膜不仅有耐腐蚀的能力，而且有一定的绝缘性，所以铝在电器制造工业、电线电缆工业和无线电工业中有广泛的用途。 (3)铝是热的良导体，它的导热能力比铁大3倍，工业上可用铝制造各种热交换器、散热材料和炊具等。 (4)铝有较好的延展性（它的延展性仅次于金和银），在100 ℃～150 ℃时可制成薄于0.01 mm的铝箔，这些铝箔广泛用于包装香烟、糖果等，还可制成铝丝、铝条，并能轧制各种铝制品。 (5)铝的表面因有致密的氧化物保护膜，不易受到腐蚀，常被用来制造化学反应器，医疗器械，冷冻装置，石油和天然气管道等。 (6)铝粉具有银白色光泽（一般金属在粉末状时的颜色多为黑色），常用来做涂料，俗称银粉、银漆，以保护铁制品不被腐蚀，而且美观。 (7)铝在氧气中燃烧能放出大量的热和耀眼的光，常用于制造爆炸混合物，如铵铝炸药（由硝酸铵、木炭粉、铝粉、烟黑及其它可燃性有机物混合而成）、燃烧混合物（如用铝热剂做的炸弹和炮弹可用来攻击难以着火的目标或坦克、大炮等）和照明混合物（如含硝酸钡68%、铝粉28%、虫胶4%） (8)铝热剂常用来熔炼难熔金属和焊接钢轨等。铝还用做炼钢过程中的脱氧剂。铝粉和石墨，二氧化钛（或其它高熔点金属的氧化物）按一定比率均匀混合后，涂在金属上，经高温煅烧而制成耐高温的金属陶瓷，它在火箭及导弹技术上有重要应用。 (9)铝板对光的反射性能也很好，铝越纯，其反射能力越好，因此常用来制造高质量的反射镜，如太阳灶反射镜等。 (10)铝具有吸音性能，音响效果也较好，所以广播室、现代化大型建筑室内的天花板等也常用铝。 但人类多吃铝，会造成脑中毒。如老年痴呆.以上是一些铝合金的资料，希望对你有所帮助。
镍和钛的金属合金，具有两种特性：形状记忆效应和超弹性
镍钛合金镍钛合金是一种形状记忆合金，形状记忆合金是能将自身的塑性变形在某些特定温度下自动恢复为原始形状的特种合金。它的伸缩率在20％以上，疲劳寿命达1×10的7次方，阻尼特性比普通的弹簧高10倍，其耐腐蚀性能目前最好的医用不銹钢，因此可以满足各类工程和医学的应用需求，是一种非常优秀的功能材料。记忆合金除具有独特的形状记忆功能外，还具有耐磨损，抗腐蚀，高阻尼和超弹性等卓越的特点。现在，我们就来总结一下镍钛合金的7种特殊性能：
形状记忆特性：形状记忆是当一定形状的母相由Af温度以上冷却到Mf温度以下形成马氏体後，将马氏体在Mf以下温度形变，经加热至Af温度以下，伴随逆相实际上形状记忆效应是镍钛合金的一个由热诱发的相变过程。
，超弹性：所谓的超弹性是指薄片在外力作用下产生远大於起弹性极限应变量的应变，在卸载时应变可自动恢复的现象。即在母相状态下，由於外加应力的作用，导致应力诱发马氏体相变发生，从而合金表现出两种普通材料的力学行为，它的弹性极限远远大於普通材料，并且不再遵守虎克定律。
抗腐蚀性能：有研究表明镍钛丝的抗腐蚀性能与不銹钢丝相仿。
抗毒性：一般情况下，表面层钛氧化物沉淀的一种屏障，使Ni-Ti合金具有良好的生物相容性。表面层的TiXOy和TixNiOy能抑制Ni的释放。
6，柔和的矫正力：目前商业上应用的牙齿矫正金属丝包括奥氏体不銹钢丝，钴-铬-镍合金丝，镍铬合金丝，钨合金丝和钛合金丝。关於这些正畸矫正金属镍钛合金的卸载曲线平台最低也最平，说明它最能提供持久柔和的矫治力。
良好的减震特性：由於咀嚼嚼和夜磨牙对於弓丝造成的振动撞击，对牙根及牙周组织的损坏程度。通过不同弓丝衰减实验的结果研究发现，不銹钢丝震动的振幅比超弹性镍钛丝大，超弹性镍钛弓丝初始振动幅度仅为不銹钢丝的一半，弓丝良好的震动和减震特性对於牙齿的健康很重要，而传统弓丝如不銹钢丝，有加重牙根吸收的倾向。
镍钛合金弹簧会随着温度的变化慢慢回缩，是因为温度发生变化时。镍钛合金要收缩。这样导致弹簧也会回缩。
（一）镍钛合金的相变与性能顾名思义，镍钛合金是由镍和钛组成二元合金，由于受到温度和机械压力的改变而存在两种不同的晶体结构相，即奥氏体相和马氏体相。 镍钛合金冷却时的相变顺序为母相（奥氏体相）-R相-马氏体相。 R相是菱方形，奥氏体是温度较高（大于同样地:即奥氏体开始的温度）的时候，或者去处载荷（外力去除Deactivation）时的状态，立方体，坚硬。形状比较稳定。而马氏体相是温度相对较低（小于Mf:即马氏体结束的温度）或者加载（受到外力活化）时的状态，六边形，具有延展性，反复性，不太稳定，较易变形。（二）镍钛合金的特殊性能1、形状记忆特性（shape memory） 形状记忆是当一定形状的母相由Af温度以上冷却到Mf温度以下形成马氏体后，将马氏体在Mf以下温度形变，经加热至Af温度以下，伴随逆相变，材料会自动恢复其在母相时的形状。实际上形状记忆效应是镍钛合金的一个由热诱发的相变过程。2、超弹性 (superelastic) 所谓的超弹性是指试样在外力作用下产生远大于起弹性极限应变量的应变，在卸载时应变可自动恢复的现象。即在母相状态下，由于外加应力的作用，导致应力诱发马氏体相变发生，从而合金表现出不同于普通材料的力学行为，它的弹性极限远远大于普通材料，并且不再遵守虎克定律。和形状记忆特性相比，超弹性没有热参与。总而言之，超弹性是指在一定形变范围内应力不随应变的增大而增大，可将超弹性分为线性超弹性和非线性超弹性两类。前者的应力-应变曲线中应力与应变接近线性关系。非线性超弹性是指在Af以上一定温度区间内加载和卸载过程中分别发生应力诱发马氏体相变及其逆相变的结果，因此非线性超弹性也称相变伪弹性。镍钛合金的相变伪弹性可达8%左右。 镍钛合金的超弹性可随着热处理的条件的变化而改变，当弓丝被加热到400ºC以上时，超弹性开始下降。3、口腔内温度变化敏感性：不锈钢丝和CoCr合金牙齿矫形丝的矫治力基本不受口腔内温度的影响。超弹性镍钛合金牙齿矫形丝的矫治力随口腔温度的变化而变化。当变形量一定时。温度升高，矫治力增加。一方面，它可以加速牙齿的运动，这是因为口腔内的温度变化会刺激由于矫治器件造成造成毛细滞息的血流停滞部位的血液流动，从而使得在牙齿移动过程中修复细胞得到充分营养，维持其生机和正常功能。另一方面，正畸医生无法精确控制或测量口腔环境下的矫治力。4、抗腐蚀性能：有研究表明镍钛丝的抗腐蚀性能与不锈钢丝相仿5、抗毒性：镍钛形状记忆合金特殊的化学组成,即这是一种镍钛等原子合金,含约50%的镍,而已知镍有致癌和促癌作用。一般情况情况下，表面层钛氧化充当了一种屏障，使Ni-Ti合金具有良好的生物相容性。表面层的TiXOy和TixNiOy能抑制Ni的释放。6、柔和的矫治力：目前商业上应用的牙齿矫形金属丝包括奥氏体不锈钢丝、钴-铬-镍合金丝、镍铬合金丝、澳大利亚合金丝、金合金丝和ß钛合金丝。关于这些正畸矫正金属丝在拉伸试验和三点弯曲试验条件的载荷-位移曲线。镍钛合金的卸载曲线平台最低也最平，说明它最能提供持久柔和的矫治力。7、良好的减震特性：由于咀嚼及夜磨牙对于弓丝造成的震动越大，对牙根及牙周组织的损害越大。通过不同弓丝衰减实验的结果研究发现，不锈钢丝震动的振幅比超弹性镍钛丝大，超弹性镍钛弓丝初始震动振幅仅为不锈钢丝的一半,弓丝良好的震动和减震特性对于牙齿的健康很重要，而传统弓丝如不锈钢丝，有加重牙根吸收的倾向。（三）镍钛合金丝的分类EvansandDurning分类法1）1940年，黄金弓丝、钴铬合金丝和不锈钢圆丝2）1960年，马氏体稳定化合金：多为镍钛合金在马氏体状态下变形后制得。该种弓丝刚度低，可产生较轻的矫治力。不存在由应力或者温度引起的马氏体相变，因此不呈现记忆效应和超弹性。3）1980年，中国镍钛合金和日本镍钛合金弓丝，为奥氏体激活合金：即在任何状态下都呈现奥氏体状态，置于口内和口外都不具有由温度引起的马氏体状态，马氏体状态只能由应力引起，具有超弹性，但是不具备形状记忆功能。该种弓丝有极佳的回弹性及较低的刚度，能产生较弱的矫治力，。作大的特点是从最初的启动到最后阶段，其产生的力持续恒定，在治疗早期牙齿不整齐时，效果较好。缺点是常温下无法弯制成型，不易焊接。若将该公司作为主弓丝，常可引起不希望的扩弓或者缩弓，且难以建立良好的前磨牙、磨牙排列。4）1990年，马氏体激活镍钛合金：即TTR低于口腔温度或者与口腔温度非常相近，在室温时以一种多元状态存在，易于变形，置于口腔内时，由应力引起的和室温引起的马氏体同时向奥氏体转变，即存在形状记忆功能和超弹性。在常温（25℃左右）及以下温度易于变形，而当达到一定温度（32℃左右）以上，又会恢复到原来预成形状，表现出形状记忆加超弹性特性。北京圣玛特科技有限公司的Smart牌和3M公司的NitinolHA牌都是典型的代表产品。热激活镍钛弓丝正因为这种特性，将其维持在常温及以下温度状态可以轻松操作成型，并安放到托槽中就位，而当在口腔中受体温热量而激活后，可产生出形状恢复力，又为矫形提供所需的力量。因热激活型镍钛矫形丝所具有的“遇冷变软，受热激活而变得弹性大”的特点，患者可以在医生的指导下，利用口含冷、热水的方式改变矫治力，更加方便了矫治者的矫正，减少了初期矫治的不适感。5）Gradedthermodynamic:增加的热力学镍钛合金：将TTR温度高于口腔温度，大概是40℃左右，这样，当镍钛弓丝置于口腔内时，仍然为多元状态，弓丝较为柔软，在口含热水时，才有奥氏体相变。因此，矫治力更加弱，可以作为成人患者和牙周病患者的初始弓丝。Omcro公司生产的含铜镍钛丝以及日本低滞后L-H镍钛弓丝便具有此种性能。（四）镍钛合金丝的临床应用：1、用于患者牙列的早期排齐整平由于镍钛合金弓丝的超弹性和形状记忆性能以及较低的应力-应变曲线，目前临床上常规将镍钛合金弓丝作为最初期纳入矫治体系的弓丝，这样，患者的不适感会大大减低。由于目前存在几种不同直丝弓矫治技术，MBT技术推荐使用0.016英寸热激活镍钛合金弓丝（HANT丝），DEMON自锁托槽技术推荐使用由Omcro公司生产的含铜的热激活镍钛合金弓丝（相变温度大概在40度左右），O-PAK矫治技术推荐使用0.016英寸超弹性镍钛合金弓丝用于早期排齐整平。2、镍钛弹簧：镍钛推簧与拉簧是一种用于牙齿正畸的弹簧，具有镍钛超弹性的特别，适合于正畸矫治开拓牙齿间的间隙和向不同方向牵拉牙齿。镍钛螺旋弹簧伸长1mm可产生大约50g的力。镍钛螺旋弹簧具有很高的弹性性能，在拉伸状态下可产生较为柔和、稳定的持续力。力的衰减很小，能产生符合临床移动牙齿所需的较理想的正畸力。符合生理要求。镍钛丝拉簧的高弹性、永久变形率极低,与相同直径的不锈钢丝相比,其释放的矫治力相差3.5-4倍。故在正畸矫治应用中,患者不仅疼痛轻,感觉力量柔和持久,且复诊时间减少,缩短了疗程,提高了疗效,是正畸治疗中的一种新的优良的力学装置。3、L-H弓丝是日本的Dr.Soma等研究开发的，由Tomy公司生产。“LH”是名自“LowHysteresis”,也就是说，当此弓丝被结扎到托槽上时，即弓丝被激活时产生的应力和移动牙齿时即弓丝慢慢恢复原状时产生的应力的差距很小。即滞后很小。SOMA等比较了LH弓丝和其他镍钛合金丝的应力应变曲线，L-H弓丝的滞后范围最小，这一特性使弓丝有低载荷和持续轻力的优势，同时该曲线初始斜度低，说明该弓丝刚度低，其余类型的镍钛合金弓丝的滞后曲线表明其刚性较大，显然L-H弓丝有明显的机械学优势。由于LH丝镍钛成分中钛的含量比例较一般镍钛弓丝高，因此将其称之为钛镍丝，并有实验证明其吸震效果较强。LH镍钛丝的另一个特点是可以弯制，并可以用热处理仪器加热定型，因此LH镍钛丝也可以从排齐整平、打开咬合到关闭间隙，以及最后的完成阶段，上下各一条弓丝即可以完成治疗，只要每一个阶段将弓丝取出弯好所需的形状，再用热处理仪器将之定形，加强硬度即可。目前在临床上使用L-H弓丝进行扩弓治疗，矫治开颌、偏颌以及反颌，因其力量的持续稳定和柔和，效果较好。同时常常配合使用J钩来改善弓丝较软的不足。虽然MEAW技术对于矫治以上错颌也有理想的效果，但繁复的弓丝弯制常使许多医师望而却步。因此有些医师改采用与力学系统类似的摇椅型镍钛弓丝加上前牙垂直牵引，虽然这样也有类似的效果，但总觉得与MEAW比较时，各个独立的牙移动的方面不如MEAW技术，原因在于摇椅型镍钛丝是一条连续的弓丝，并且亦没有办法弯折。因此，托槽粘接的角度与弓丝的摇椅曲度决定了每一颗牙齿的角度，不像MEAW技术中每一个牙齿的角度较有个别调整的空间。使用LH镍钛弯上摇椅，再用弓丝成形器在口内弯折后倾弯或者前倾弯，效果相当理想。
镁合金成形技术研究进展熊守美1 , 苏仕方2(11 清华 - 东洋镁铝合金成形技术研究开发中心 , 清华大学机械工程系 100084 ; 21 中国机械工程学会铸造分会 ,辽宁沈阳 110022)摘要: 镁合金材料及其成形技术的研究和开发对于扩大镁合金在我国的应用具有十分重要的意义。根据第四届中国国际压铸会议论文资料, 综述了国内外镁合金材料及其成形技术的的国内外发展趋势, 包括材料、成形技术及数值模拟等, 展望了镁合金的开发与应用前景。关键词: 镁合金; 材料; 成形技术; 数值模拟中图分类号: TG24912 ; TG14612 2 文献标识码: A 文章编号: 100124977 (2005) 0120020204+Research Progress on Processing Technologyof Magnesium AlloysXIONG Shou2Mei1 , SU Shi2Fang2(11Tsinghua2TOYO R &D Center of Magnesium and Aluminum Alloys Processing Technology , Departmentof Mechanical Engineering , Tsinghua University , Beijing 100084 , China ; 21Foundry Institution of ChineseMechanical Engineering Society , Shenyang 110022 , Liaoning , China)Abstract : Research and development of magnesium alloys and their processing technology are of greatimportance in promoting domestic applications of magnesium alloys in China. Based on the conferencepapers of the 4th China International Die casting Congress & Exhibition , this paper reviewed the trend ofresearch and development of magnesium alloys and their processing technology at home and abroad , in2cluding materials development , processing technology , and numerical simulation technology , etc. At thesame time , the prospect for magnesium applications was also discussed.Keywords : magnesium alloy ; materials ; processing technology ; numerical simulation镁合金正被广泛用于汽车、航空、电子以及消费原因 , 使它难以作为关键零部件 (如发动机零件) 材品工业中的各种结构件。尽管这些应用的增长主要受料在汽车等工业中得到更广泛的应用。同时镁合金密重量减轻的驱动 , 但是 , 镁合金的其它优点也起着重排六方的晶体结构决定了其塑性变形能力较差 , 如何要的作用。其一 , 是它们对压铸工艺的独特适应性 ,解决这一问题是镁合金应用的关键之一。针对上述问可以高速生产近终形零件; 其二 , 优良的模具寿命所题 , 研究人员取得了以下进展。节约的生产成本 , 可以弥补其原材料价格比铝合金稍111 压铸镁合金材料开发贵的不足 , 增强与压铸铝合金的竞争力; 此外 , 极好针对商用压铸镁合金抗高温蠕变性能较差的现状 , 以的可加工性能和减振性能也是镁合金具有的重要性AZ 91 合金为基准合金 , 一汽铸造研究所的研究人能。中国现在是世界上最大的镁生产及出口国 , 但镁员〔1〕进行了抗高温蠕变压铸镁合金的开发。论文讨合金在中国工业 , 尤其是汽车工业中的应用仍很有论了稀土元素 Ce , Y, Nd 以及 Ca 和 Si 的添加对压限。因此 , 深入开展镁合金及其成形技术的研究开铸镁合金在常温拉伸性能以及 150 ℃条件下的蠕变行发 , 对于扩大镁合金在中国工业中的应用具有十分重为 , 显微组织的影响 , 以及对表面处理和腐蚀试验的要的意义。影响 , 并进行了实际产品的生产。在第四届中国国际压铸会议的 50 余篇学术论文该文综合考虑合金的化学成分、合金元素的固溶中 , 涉及镁合金及其成形技术的相关论文、学术报告度、各种金属间化合物 , 在保持 AZ 91 合金基本成分有 10 余篇 , 本文将从镁合金材料、成形工艺 , 镁合不变的条件下 , 设计了四组试验合金进行考查。采用金熔体保护及镁合金成形过程数值模拟等方面总结会挤压的方法试制了 30 种成分合金试棒 , 对试棒的常议论文所涉及的相关领域的研究进展。温力学性能和腐蚀行为进行了测试 , 并初步考查了铸造性能和蠕变抗力。通过试验 , 开发的新合金性能接1 镁合金材料研究近德国大众公司开发的 MRI2153 合金 , 合金工艺性能耐热性及疲劳性能是阻碍镁合金广泛应用的主要与 AZ 91 合金相当 , 可以采用与 AZ 91 合金相同的生收稿日期: 2004211220 收到初稿 , 2004211229 收到修订稿。作者简介: 熊守美 (1966 - ) , 男 , 湖北麻城人 , 博士 , 博士生导师 , 主要从事压铸工艺和技术方面的研究。E2mail: smxiong @tsinghua1edu1cn铸造熊守美等: 镁合金成形技术研究进展·21 ·产工艺。在采用沈阳应用化学研究所低成本的电解镁造四大方面为主。其中压铸仍为最主要的成型工艺 ,- 稀土中间合金情况下 , 有效地控制了成本。在蠕变我国镁合金压铸件产量由 1995 年的 1 562 t 提高到试验中发现 , Mg2Al2Re2Zn 体系中的强化相 Al11Ce3 在2002 年的 4 950 t , 7 年里产量增长了 2 倍多 , 平均少量 Ca 存在下稳定性可以进一步提高。Nd 和 Y的添年增长率达 18 %。利用镁合金压铸件代替传统铸铁、加不会使 AZ 91 合金的晶粒度改变 , 但可以产生固溶铸钢件 , 甚至代替铝压铸件 , 正成为制造业特别是汽强化 , 具有极佳的蠕变性能。车制造业的发展趋势〔4〕。112 压铸镁合金的低周疲劳行为研究211 镁合金压铸沈阳工业大学的研究人员〔2〕通过试验发现: 压目前 , 镁合金压铸工艺的研究热点主要集中在两铸态 AZ 91 疲劳寿命最低; 在高应变幅条件下 , 压铸大方面: 镁合金压铸零件的开发设计和镁合金压铸工态 AM50 + Nd 疲劳寿命高于镁合金 AZ 91 , 在较低艺的完善创新。随着模具设计水平和压铸零件性能的应变幅条件下 , 压铸态 AM50 + Nd 的寿命要低于经提高 , 镁合金压铸件的应用领域已经从传统的笔记本过固溶处理的 AZ 91 的疲劳寿命; 经过固溶处理的电脑外壳、手机外壳等表面覆盖件发展到了发动机支AZ 91 镁合金的过渡疲劳寿命明显高于压铸态 , 压铸架、轮毂、框架件等受力部件以及安全部件。态 AM50 + Nd 镁合金的过渡寿命要高于压铸态 AZ相应地 , 为了满足不断提升的零件性能要求 , 随91。经过固溶处理以后 AZ 91 中的β相消失 , 使材料着材料科学和其他科学技术的进步 , 在传统压铸工艺的延展性增加 , 循环硬化程度有所降低。的基础上衍生出了真空压铸、充氧压铸、超低速压铸113 镁合金的铸态组织研究等诸多分支技术。其中真空压铸以其极低的铸件含气镁铝合金在未经变质处理时 , 铸态下晶粒尺寸可量、较好的设备兼容性和优异的铸件性能等优点得到达 3 ×10 ～5 ×10 m , 组织很粗大。合金的组织决2424了高度重视和大力发展。众所周知 , 压铸件的气孔问定性能 , 性能决定合金的应用 , 以往镁合金的组织控题是限制其性能提高的主要瓶颈。真空压铸在传统压制主要是为了提高其塑性变形能力。因为镁合金为密铸工艺周期上耦合真空系统抽除型腔气体 , 是一种减排六方 , 这就决定了其塑性变形能力较差。而实践证少压铸件气孔 , 去除铸模内气体和润滑剂蒸汽的有效明 , 细小等轴晶可以改善镁合金的塑性变形能力。而方法。目前研究的热点是如何在型腔内得到更高的真半固态触变成形也要求初始的铸态组织应为细小的等空度 , 及相应的模具密封工艺。高真空压力铸造得到轴晶组织 , 因此如何控制镁合金的组织是镁合金半固的零件不仅可以大大降低微孔和气孔等铸造缺陷 , 还态成形的关键之一。可以进行热处理和压铸焊接〔5〕。常用的镁合金组织控制工艺主要有液态处理法和沈阳工业大学的研究人员〔6〕研究了压铸镁合金固态处理法两大类。液态处理法由于简单、易于实轮毂缺陷的产生原因 , 通过对浇注系统和零件结构的现 , 不外加额外设备等 , 在工业应用中具有广阔的空改进及压铸工艺参数的调整 , 有效地仿真了缺陷的产间。液态处理法包括添加晶粒细化剂法、过热处理生 , 明显改善了压铸镁合金轮毂件的质量。法、熔体搅拌法两大类。固态处理法包括等静角压清华大学的研究人员〔7〕与一汽合作 , 系统地研(ECEA) 法、大比率挤压法和铸造粉末法。但对以究了各种压铸工艺参数对镁合金压铸件质量的影响规上这些方法的机理还不是很清楚或是方法正处于试验律 , 成功开发了一汽集团首件镁合金压铸件并投入实阶段。对镁合金的组织控制机理缺乏了解 , 产生了一际生产。目前 , 正进行镁合金真空压铸及超低速压铸些混淆 , 导致工业中对镁合金的组织控制主要依靠经的实验研究。验的方法〔3〕。到目前为止 , 对镁合金组织控制的研212 低压铸造究 , 主要集中于外来质点对形核的促进作用、抑制晶低压铸造由于其充型过程的平稳性和良好的排气粒生长的作用和溶质对形核率的影响。在镁合金熔体性能 , 被广泛应用于轮毂等对铸件缺陷较为敏感的零中加入少量的孕育剂 (MgCO3、C2Cl6、FeCl3 等) 或件制造。而传统低压铸造工艺所采用的压缩空气 , 由溶质原子 (Zr、Ca、Sr、RE 等) , 能细化镁合金的铸于气体纯度不够及氧的分压过高所造成的氧化和吸气造组织并改变沉淀物的形貌 , 提高镁合金的力学性等问题会造成铸件的氧化夹杂、微裂纹、缩孔和缩松能 , 改善压力加工性能。但是 , 镁合金组织细化的研等铸造缺陷 , 限制了低压铸造的推广。采用电磁泵充究和应用远不如铝合金的深入 , 值得进一步研究。型的低压铸造新工艺技术 , 以电磁泵充型技术为核心 , 在加压充型和保压时 , 采用非接触式的电磁力直2 镁合金成形技术研究开发接作用于液态金属 , 实现了铝液的平稳输送和充型 ,当前 , 镁合金的成型工艺仍然以 压 力 铸 造并防止由于紊流所造成的二次污染 , 得到了较高的铸(HPDC) 、低压铸造 (L PDC) 、挤压铸造和半固态铸件质量。同时引入计算机控制系统 , 提高了工艺执行Jan. 2005·22 ·FOUNDRYVol154 No11的准确度 , 也使生产效率得到了提升〔8〕。此外 , 由体保护原理的基础上 , 讨论了各种混合气体保护的缺于电磁泵低压铸造工艺所采用的开环控制方式对控制点 , 研究了不同配比、不同的温度和操作条件下精度具有较高的要求 , 针对工艺参数的测定和电磁设HFC2134a 气体对液态镁合金的保护效果 , 并且研究备的开发也展开了一系列研究工作〔9- 10〕。了相关工艺参数和防护工艺。研究结果认为 HFC2213 半固态铸造134a 气体相对于 SO2 和 SF6 具有更优良的保护特性 ,半固态铸造工艺自诞生以来一直受到了广泛的关可作为镁合金熔体气体保护的一种优先选择。注 , 处于研究的前沿。由于该项技术对设备依赖性较4 镁合金压铸过程数值模拟大 , 目前研究重点主要集中在设备性能的提升和完善上。新开发的第二代触变成形机 , 最高射出速度达到在镁合金压铸生产过程中 , 液态或半固态的金属5 m/ s , 其螺杆、套筒等关键部件采用新型合金 , 耐在高速、高压下充型 , 并在高压下迅速凝固 , 容易产高温及热传导性能有所提升 , 锁模机构的刚性和速度生气孔等铸造缺陷。由于镁合金压铸充型速度比铝合得到加强 , 降低了能耗 , 得到了更高的铸件质量和生金更高 , 凝固速度更快 , 因此 , 镁合金压铸对模具的产效率〔11〕。与此同时 , 针对触变成形法的研究也促流道系统及热平衡设计提出了更高的要求。充分了解使了一批新技术的投入使用 , 如热流道系统、长喷嘴充填过程的流动和换热规律 , 设计合理的铸件、铸型技术、触变成形锻压工艺等。结构及浇注系统 , 选择恰当的压铸工艺参数 , 不仅可214 挤压铸造以降低铸件废品率 , 提高铸件质量和生产效率 , 而且挤压铸造在镁铝合金材料领域 , 以其高铸件质可以延长模具的使用寿命。数值模拟方法为解决上述量、高力学性能和高致密度得到了密切的关注。挤压问题提供了有效的手段。通过压铸充型过程流场、温铸造可以使任何壁厚的零件进行固溶热处理 , 从而得度场的数值模拟 , 能够较准确地表达压铸充型过程的到高于常规压铸的力学性能。另一方面 , 挤压铸造可流动和传热规律 , 实现理想的型腔充填状态及模具热以利用在凝固过程中加压的方法 , 得到优于低压铸造平衡状态 , 预测可能产生的卷气、冷隔等缺陷 , 进而的铸件致密结构。同时 , 挤压铸造和半固态铸造的密优化压铸工艺 , 对实际压铸生产具有重要的指导意切联系也使这项技术处于研究的热点。目前挤压铸造义。因而 , 计算机模拟仿真技术被广泛用于镁合金压面临的主要问题是对技术和过程控制要求过高 , 要求铸件的模具设计及工艺分析。的投资比较高。目前的研究重点主要集中在挤压顶清华大学的研究人员〔4〕长期从事压铸过程模拟针、吸热棒的运用 , 挤压位置的选择 , 工艺参数的控仿真技术的研究工作 , 并成功将模拟仿真技术用于镁制等方面〔12〕。合金压铸件的模具设计优化、热平衡分析及模具热应挤压铸造既可以采用专用设备进行生产 , 也可以力和变形的分析。同时 , 特别对压室中的液态金属流在常规压铸机上进行。他解决了传统压铸机不能生产动进行了模拟 , 系统地研究了低速压射速度及压室充厚大件 , 压铸件普遍存在的缩孔缩松问题 , 可生产各满度等参数对压室中的气体卷入 , 并在此基础上提出种不同强度和流动性的合金 , 简化了压铸模具设计的了低速压射的优化工艺。思路 , 降低了简单零件的压铸模具成本 , 使得中小批沈阳工业大学的研究人员〔15- 16〕采用 FLOW3D量零件使用压铸工艺生产变成可能。以挤压铸造技术对不同镁合金铸件的充型过程及凝固过程进行了模拟为基础 , 对常规铸造、低压铸造和传统挤压铸造机进分析 , 为镁合金压铸件模具设计及预测缺陷位置提供行的改造为挤压铸造技术的推广做出了贡献〔13〕。了理论指导 , 有效地提高了镁合金压铸件质量及降低模具设计成本。3 镁合金熔体保护5 结束语镁及镁合金的气体保护熔炼技术是目前生产高纯度、高品质镁合金的技术关键。20 多年前 , 在熔炼随着镁合金压铸件的广泛应用 , 提高其压铸性能镁和镁合金时采用 SF6 做保护气体 , 是当时镁工业界和抗高温蠕变性能已成为当前重要的研究课题。我国最大的进步。因为它消除了以前使用 SO2 和熔剂熔的稀土资源丰富 , 稀土镁合金的性能优良 , 开发具有炼所产生的大多数问题。但到了 1990 年 , SF6 和类中国特色的压铸稀土镁合金 , 提高其抗高温蠕变性似物的高温室效应 (是 CO2 的 24 000 倍 , 并能在大能 , 具有重要意义。气中长期存在 3 200 年) 迫使镁工业用户必须寻找技压铸是镁合金最主要的成形工艺 , 为了进一步提术上可行 , 经济、环保的替代保护气体。寻找 SF6 的高镁合金零件的的质量及扩大镁合金的应用领域 , 应替代保护气体是目前镁工业界的一个重要课题。积极开展一些新的成形工艺方法 (如真空压铸、超低华北工学院的研究人员〔14〕在论述镁合金熔体气速压铸、挤压铸造、半固态铸造等成形方法) 的基础铸造熊守美等: 镁合金成形技术研究进展·23 ·研究工作。镁合金成形技术对工艺过程提出了更高的四届中国国际压铸会议论文集 〔C〕. 北京: 机械工业出版社 ,要求 , 采用数值模拟技术可以优化成形工艺 (模具设2004. 35 - 39〔9〕 许音 , 彭有根 , 杨晶. 直流电磁泵低压铸造系统工艺参数测定计) , 控制模具热平衡 , 提高产品质量和降低废品率。〔A〕. 第四届中国国际压铸会议论文集〔C〕. 北京: 机械工业出版社 , 2004. 84 - 88参考文献:〔10〕 刘云 , 杨晶 , 党惊知. 磁铁结构参数对电磁泵磁场强度的影响〔1〕 刘海峰 , 佟国栋 , 侯骏 , 等. 含稀土抗蠕变压铸镁合金的开发〔A〕. 第四届中国国际压铸会议论文集〔C〕. 北京: 机械工业〔A〕. 第四届中国国际压铸会议论文集 〔C〕. 北京: 机械工业出版社 , 2004. 103 - 108出版社 , 2004. 145 - 155〔11〕 李博文. 新一代触变成形机特点〔A〕. 第四届中国国际压铸会〔2〕 申健 , 洪成森 , 李锋 , 等. AZ91 与 AM50 + Nd 镁合金的低周议论文集〔C〕. 北京: 机械工业出版社 , 2004. 40 - 46疲劳行为〔A〕. 第四届中国国际压铸会议论文集 〔C〕. 北京:〔12〕 夏云 , 里奇·杰卡斯 , 马克·亨特. 挤压铸造及其过程和质量控机械工业出版社 , 2004. 133 - 138制技术〔A〕. 第四届中国国际压铸会议论文集〔C〕. 北京: 机〔3〕 李元东 , 郝远 , 陈体军 , 等. 镁合金的铸态组织控制工艺与机械工业出版社 , 2004. 47 - 54理〔A〕. 第四届中国国际压铸会议论文集〔C〕. 北京: 机械工〔13〕 欧阳明. 从普通压铸、挤压、低压铸造机的改造认识挤压压铸业出版社 , 2004. 156 - 161技术〔A〕. 第四届中国国际压铸会议论文集〔C〕. 北京: 机械〔4〕 唐玉林 , 苏仕方 , 徐爽. 从世界压铸工业及市场发展看我国压工业出版社 , 2004. 109 - 115铸工业〔A〕. 第四届中国国际压铸会议论文集. 北京: 机械工〔14〕 靳玉春 , 郭琪敏 , 许小忠 , 等. 液态镁合金气体保护方法研究业出版社 , 2004 , 1 - 10发展趋势〔A〕. 第四届中国国际压铸会议论文集〔C〕. 机械工〔5〕 Mamoru Murakami , Hiroyuki Omura. High vacuum die cast tech2业出版社 , 2004. 167 - 172nology and its application〔A〕. 第四届中国国际压铸会议论文集〔15〕 张艳 , 吴伟 , 等. 镁合金压铸充型过程的优化〔A〕. 第四届中〔C〕. 北京: 机械工业出版社 , 2004. 16 - 20国国际压铸会议论文集〔C〕. 北京: 机械工业出版社 , 2004.〔6〕 于宝义 , 王峰 , 刘正 , 等. 压铸镁合金轮毂缺陷分析与解决措25 - 30施〔A〕. 第四届中国国际压铸会议论文集〔C〕. 北京: 机械工〔16〕 洪成淼 , 申健 , 等. 镁合金压铸件缺陷的计算及模拟仿真分析业出版社 , 2004. 173 - 179〔A〕. 第四届中国国际压铸会议论文集〔C〕. 北京: 机械工业〔7〕 熊守美. 镁合金压铸成形技术研究进展〔R〕. 第四届中国国际出版社 , 2004. 226 - 230压铸会议学术报告 , 2004〔8〕 侯击波 , 霍立兴 , 程军. 电磁泵低压铸造控制系统研究〔A〕. 第(编辑 : 曲学良 , qxl @foundryworld1com)
合金耐腐蚀性比镁好镁会与空气接触反应生成氧化膜而合金会与空气有较少接触
镁合金的优越性目前3C产品外壳大都使用塑胶材料（如PC、ABS、PC/ABS或添加纤维等）。一般厚件3C产品（厚度2.5-3.2mm,长度比<100），可用射出成型或气体辅助成型制作，但厚度太大或长度比太小，会产生喷泉流现象，造成产品外观瑕疵且应力分布不均，致使产品强度减弱。而目前3C产品外壳有越来越薄的趋势，以薄壳成型来制作，当肉厚低于1mm时，产品刚性及耐冲击性的要求快速上升。如此，一般塑料材料已不适用，若添加纤维来增强强度，散热及电磁遮蔽、产品耐冲击性又差。因此，为解决以上问题，选择另类材料及新的加工工艺将成为必然。镁合金在此情况下脱颖而出。一、镁合金的特点： 轻量化 镁合金比重为铝合金的68%，锌合金的27%，钢铁的23%，所以它在所有结构用合金中属于最轻者。因此镁合金适用于汽机车零件、机械零件、3C产品外壳、建筑材料等产品。极佳的电磁遮蔽性手机及电脑的金属外壳能提供优越的抗电磁保护作用。一般而言，轻的电脑外壳采用不支持电磁遮蔽的塑料，它需要再加工或喷层导电漆来达到电磁遮蔽性的要求。镁合金外壳能够完全吸收频率超过100dB的电磁干扰。极佳的热传导性及热扩散性 一般来讲，笔记本电脑的电力消耗大约20至30瓦。因此，热传导是考虑系统稳定的一个主要因素。在笔记本电脑内，CPU能达到最高温度。因此，为了防止电脑温度过高，我们就必须防止CPU过热。通常，笔记本电脑的设计者选择导热管加风扇来使系统降温，但是随着CPU频繁地升级，这种方法将不能有效地降低系统的温度并会导致一些设计上的问题，比如更大的电力消耗以及空间不够。根据最近的测试报告，镁合金的热传导性是塑料的100倍，所以如果选择镁合金外壳，过热的问题就会得到缓和与解决。刚性高，耐冲击 镁合金具有多方面的优势。尽管它的比重要比塑钢轻,但它的强度和刚性都要比塑钢强得多。根据测试报告，对镁合金笔记本电脑外壳的耐冲击性测试如下：1 将一米高五磅重东西以自由落体的方式撞击镁合金笔记本电脑外壳，镁合金外壳可以承担它的撞击，而不造成损伤；2 将镁合金外壳的笔记本电脑从一米高的地方落下，镁合金外壳不容易破裂，而且因为具有防震效果，所以能够保护内部零件。耐蚀性佳镁合金的耐蚀性（在盐腐蚀试验中）是碳钢的8倍，铝合金的4倍，更是塑料材料的10倍以上，防腐能力是合金中最佳者。美好的质感自上世纪起，人类对金属质感、光泽仍有不可抹减的爱恋，多种品牌型号的手机外壳做成类金属样式，但其光泽仍与金属有差距，质感更不同于金属。但镁合金作为金属，外观及质感极佳，对于工业设计师而言，这是不可忽略的事实。费用考虑 尽管塑料比镁便宜，但使用塑料的笔记本电脑外壳需要制作得厚些（超过2mm）以便保持坚固性。在使用后，由于内部温度的上升，塑料常产生软化作用，不足以达到支撑的强度。这就迫使设计者常在塑料内部增加金属支撑框体，以保护内部零件。且成型以后，工程塑料仍需作电镀或加金属薄膜以使它具备抗电磁干扰功能。这些工序都会大量增加采用塑料外壳的成本。镁合金外壳可以被制作得更薄些（在0.35mm到1mm之间）并且外观方面它也可以烤漆或电镀过程。尽管有一些外壳的成本可能会比塑料高些，但是经过一些合适的设计，如不用埋螺丝，不用不锈钢支撑，不用导电漆等等； 及专业的生产控制，它的成本可以与塑料一样。同时，与铝合金，锌合金来做成本比较，它还是低成本的材料，并且还可以提供了一些附加的价值，比如可以给人一种高档及高科技产品的外观形象。环保产品 塑料产品超过使用寿命，大部分不能回收，变成万年垃圾与废物。这引起了环境保护的广泛关注。越来越多的国家已经立法来限制塑料的使用或者让生产商来承担塑料产品报废后的回收处理。而镁合金不同，它可以完全回收，其回收价值是钢制品的十倍。当工业发展到一定程度，将会有回收厂来处理用完的产品。因此，对消费性生产厂商来说，用镁合金有很多有利的衍生效果。超薄—美学的设计 是超薄型的材料，一般的厚度都在0.35mm到1mm之间，但在塑料生产里，在2.54mm以下。这个薄度对塑料来说很难达到，而以铝合金来说，光外壳的厚度大约就是2mm以上。而镁合金外壳的厚度可以降到1mm甚至更薄。正因为这一点，对镁合金来说，要保持机壳的总厚度在2.54mm以下要容易的多。因此，大多数超薄笔记本电脑以及手机外壳正在采用镁合金材料作外壳。优良的压铸及后加工技术本公司优良的镁合金压铸制造技术已经使得3C产业使用镁合金外观件及内部结构件成为一种发展趋势。随着产业的不断扩大和生产良率的不断提高，镁合金将会变得很流行，各种设计与外观都已达到技术成熟的地步，并且将会被继续广泛应用。不可燃性 电子产业的应用，工程塑料已经考虑到了燃烧问题。但是镁合金熔点达427℃，和塑料相比，它具有很好的不可燃性，尤其是使用在汽机车零部件以及建筑材料上，可以避免瞬间的燃烧。稳定的资源 镁在地壳中的储量居第八位，大部分的镁原料自海水中提炼，所以它的资源是稳定的、充分的，绝对不虞匮乏。 我们是镁合金专业工厂，如果你要更了解镁合金，请登录我们的网站《》
铝合金：铝合金材料的应用有以下三个方面：一是作为受力构件；二是作为门、窗、管、盖、壳等材料；三是作为装饰和绝热材料。利用铝合金阳极氧化处理后可以进行着色的特点，制成各种装饰品。铝合金板材、型材表面可以进行防腐、轧花、涂装、印刷等二次加工，制成各种装饰板材、型材，作为装饰材料。 这个可以么？可以的话把分给我吧~嘿嘿还有：铝合金: 铝合金是纯铝加入一些合金元素制成的，如铝—锰合金、铝—铜合金、铝—铜—镁系硬铝合金、铝—锌—镁—铜系超硬铝合金。铝合金比纯铝具有更好的物理力学性能：易加工、耐久性高、适用范围广、装饰效果好、花色丰富。铝合金分为防锈铝、硬铝、超硬铝等种类，各种类均有各自的使用范围，并有各自的代号，以供使用者选用。 铝合金仍然保持了质轻的特点，但机械性能明显提高。铝合金材料的应用有以下三个方面：一是作为受力构件；二是作为门、窗、管、盖、壳等材料；三是作为装饰和绝热材料。利用铝合金阳极氧化处理后可以进行着色的特点，制成各种装饰品。铝合金板材、型材表面可以进行防腐、轧花、涂装、印刷等二次加工，制成各种装饰板材、型材，作为装饰材料。 铁合金: 品种用途 作为炼钢脱氧剂，应用最广泛的是锰铁和硅铁。强烈的脱氧剂为铝(铝铁)、硅钙、硅锆等（见钢的脱氧反应）。用作合金添加剂的常用品种有：锰铁、铬铁、硅铁、钨铁、钼铁、钒铁、钛铁、镍铁、铌(钽)铁、稀土铁合金、硼铁、磷铁等（表1 常用铁合金）。各种铁合金又根据炼钢需要，按合金元素含量或含碳高低规定许多等级，并严格限定杂质含量。含有两种或多种合金元素的铁合金叫做复合铁合金，使用这类铁合金可同时加入脱氧或合金化元素，对炼钢工艺有利，且能较经济合理地综合利用共生矿石资源。常用的有：锰硅、硅钙、硅锆、硅锰铝、硅锰钙和稀土硅铁等。 炼钢用纯金属添加剂有铝、钛、镍和金属硅、金属锰、金属铬等。某些易还原的氧化物如MoO□、NiO,也用于代替铁合金。此外，还有氮化铁合金，如经过氮化处理的铬铁、锰铁等，以及混有发热剂的发热铁合金等。 铜合金: 黄铜 以锌作主要添加元素的铜合金，具有美观的黄色，统称黄铜。铜锌二元合金称普通黄铜或称简单黄铜。三元以上的黄铜称特殊黄铜或称复杂黄铜。含锌低於36％的黄铜合金由固溶体组成，具有良好的冷加工性能，如含锌30％的黄铜常用来制作弹壳，俗称弹壳黄铜或七三黄铜。含锌在36～42％之间的黄铜合金由和固溶体组成，其中最常用的是含锌40％的六四黄铜。为了改善普通黄铜的性能，常添加其他元素，如铝、镍、锰、锡、硅、铅等。铝能提高黄铜的强度、硬度和耐蚀性，但使塑性降低，适合作海轮冷凝管及其他耐蚀零件。锡能提高黄铜的强度和对海水的耐腐性，故称海军黄铜，用作船舶热工设备和螺旋桨等。铅能改善黄铜的切削性能；这种易切削黄铜常用作钟表零件。黄铜铸件常用来制作阀门和管道配件等。 青铜 原指铜锡合金，后除黄铜、白铜以外的铜合金均称青铜，并常在青铜名字前冠以第一主要添加元素的名。锡青铜的铸造性能、减摩性能好和机械性能好，适合於制造轴承、蜗轮、齿轮等。铅青铜是现代发动机和磨床广泛使用的轴承材料。铝青铜强度高，耐磨性和耐蚀性好，用於铸造高载荷的齿轮、轴套、船用螺旋桨等。铍青铜和磷青铜的弹性极限高，导电性好，适於制造精密弹簧和电接触元件，铍青铜还用来制造煤矿、油库等使用的无火花工具。 白铜 以镍为主要添加元素的铜合金。铜镍二元合金称普通白铜；加有锰、铁、锌、铝等元素的白铜合金称复杂白铜。工业用白铜分为结构白铜和电工白铜两大类。结构白铜的特点是机械性能和耐蚀性好，色泽美观。这种白铜广泛用於制造精密机械、化工机械和船舶构件。电工白铜一般有良好的热电性能。锰铜、康铜、考铜是含锰量不同的锰白铜，是制造精密电工仪器、变阻器、精密电阻、应变片、热电偶等用的材料。
一、防锈铝合金防锈铝合金包括铝-镁系和铝-锰系合金以及工业纯铝。防锈铝合金的牌号及化学成分见表6-2。这类铝合金的主要性能特点是具有优良的耐蚀性能，因而得名防锈铝合金，简称为防锈铝。此外，还具有良好的塑性与焊接性，适宜压力加工和焊接。这类合金不能进行热处理强化，力学性能比较低。为了提高其强度，可用冷加工方法使其强化。但由于防锈铝的切削加工工艺性差，故适用制作焊接管道、容器、铆钉以及其他冷变形零件。1.铝-镁系合金铝-镁系合金的化学成分中，镁是合金的主要组成元素，此外，还加入少量锰、钛等其他元素。镁含量对合金力学性能的影响是随着镁含量的增加，合金的强度、塑性亦相应提高。但是，当合金中的镁含量超过5%Mg时，合金的抗应力腐蚀性能降低；当镁含量超过7%时，合金的塑性降低，焊接性能也变坏。这可能是与镁含量增加使合金在液态结晶时成分偏析倾向增大有关。由于合金不平衡结晶的结果，合金组织中出现脆性的β(Mg2Al3)相，而导致铝-镁合金性能变坏。实验指出，在镁含量较低的5A02和5A03合金中没有发现β(Mg2Al3)相，随着镁含量的增加，在5A05中可以看到少量β(Mg2Al3)相，而在5A06 合金中，由于镁含量增加，β(Mg2Al3)相的数量亦相应的增加。铝-镁合金中加入少量（0.3%～0.8%）锰，不仅能改善合金的耐蚀性，而且还能提高合金的强度。少量的钛或钒主要是起细化晶粒的作用，少量硅可以改善合金的焊接性能。在铝-镁系防锈铝中，铁、铜和锌等是有害的杂质元素，它们能使合金的耐蚀性能与工艺性能恶化，故其含量应严格控制。在铝-镁合金中，镁在固态铝中虽然有较大的溶解度，且随温度变化亦比较大，但由于铝-镁合金淬火后，在时效过程中形成的过渡相β′与基体不发生共格关系，其时效强化效果甚微，故铝-镁系合金含7%以下的防锈铝均不采用时效处理来提高强度。为了提高铝-镁系防锈铝的强度，可以采用冷加工硬化的方法使其强度提高。但是，含镁高的铝-镁系防锈铝在冷加工硬化后，随着在室温放置时间的增长，合金的强度、特别是屈服强度明显下降，而延伸率显著提高。而且，这种软化现象随着合金的镁含量和变形度增加而表现得更明显。为了防止高镁防锈铝冷加工后的软化现象，冷变形后应进行稳定化处理，即加热到150℃保温3小时，使之在室温下力学性能稳定化。2.铝-锰系防锈铝铝-锰系防锈铝中常见的合金牌号是3A21。锰是该合金的主要组成元素，锰含量在1.0%～1.6%范围内的合金具有较高的强度，同时具有较高的塑性、焊接性以及优良的耐蚀性。当锰的含量超过1.6%时，由于形成大量的脆性化合物MnAl6，虽然强度有所提高，但合金的塑性显著降低，压力加工工艺性能变坏，故防锈铝中锰含量一般不超过1.6%。铁和硅是合金中的主要杂质。铁降低锰在铝中的溶解度，并能溶于MnAl6中，形成（FeMn）Al6，这是硬而脆的难溶相。实践证明，合金中含有少量铁能细化合金组织，但铁含量过高时，则由于形成大量的（FeMn）Al6相，而显著降低合金的力学性能与工艺性能，降低铸造性，故应严格控制其含量，一般控制在0.6%以下。铝-锰系防锈铝因其时效强化效果不佳，故不采用时效处理。3A21合金制品的热处理主要是退火。但3A21合金退火时，极易产生晶粒粗大，导致合金半制品在深冲或弯曲时表面粗糙或产生裂纹。为了保证获得细晶粒的3A21合金制品，应提高退火时的加热速度，或在合金中加入少量钛的同时，加入0.4%铁来细化合金组织。或者将铸锭在600～620℃进行均匀化退火，消除锰在晶内和晶间的严重偏析。从而获得均匀细小的晶粒，以改善压力加工工艺性能。二、硬铝合金铝-铜-镁系合金是使用较早，用途很广的铝合金。它有强烈的时效强化作用，经时效处理后具有很高的硬度、强度，故铝-铜-镁系合金总称为硬铝合金。此外，这类合金还具有优良的加工工艺性能，可以加工成板、棒、管、线、型材及锻件等半成品，广泛应用在国民经济和国防建设中。硬铝合金的主要合金元素是铜、镁，此外还含有锰和一些杂质元素铁、硅、镍、锌等。硬铝合金的牌号及化学成分见表6-2。不同牌号的硬铝合金具有不同的化学成分，其性能特点亦不同。含铜、镁量低的硬铝强度较低而塑性高；含铜、镁量较高的硬铝则强度高而塑性较低。硬铝合金的成分与力学性能的关系，是由合金中形成的强化相所决定的。硬铝合金中铜与镁比值不同，形成的强化相亦不同，其强化相与强化效果亦不同。镁含量低时，形成的主要强化相是θ相(CuAl2)，当镁量增加时，θ相减少，而形成强化效果比θ相更大的、并具有一定耐热性的S(Al2CuMg)相。进一步增加镁含量，则相继形成强化效果较差的T(Al6CuMg4)相与β(Al3Mg2)相。当铜与镁的比值一定时，铜和镁总量愈高，强化相数量愈多，强化效果愈大。在硬铝合金中除主要元素铜和镁外，还加入一定量的锰。锰能改善硬铝的耐蚀性，细化合金组织，淬火是锰溶于固溶体起固溶强化作用，使淬火硬铝的强度提高30~70MPa。但含锰量过高时塑性显著降低，因此，硬铝合金中的锰含量控制在0.3%～1.0%。此外，锰还能提高硬铝的耐热性能和削弱杂质铁的有害作用。硬铝合金中的锰含量控制在0.3%～1.0%。铁是硬铝中的有害元素，它不仅能与铝形成金属间化合物FeAl3，降低合金的塑性与耐蚀性能，而且还能夺取合金中的铜形成Cu2FeAl7难溶化合物，减少强化相θ和S的数量，降低时效强化效果。此外，铁还能与硅、锰等元素形成粗大的脆性化合物，使工艺性能变差。因此，在硬铝合金中铁含量一般都控制在0.5%以下。硅在硬铝中亦是以杂质存在。当合金中铁含量较低时，硅与镁优先形成Mg2Si化合物，消耗一部分镁，使强化相S(Al2CuMg)相减少。从而降低硬铝的自然时效强化效果。硅对硬铝的塑性没有太大的影响，相反当合金中有铁存在时，硅与铁形成Fe2SiAl2相，可以减少由于形成粗大片状的(FeMn)Al2相的是有害元素，作用。在硬铝中硅的含量一般控制在0.5%～0.7%。镍在硬铝合金中亦是有害杂质。镍能与铜形成AlCuNi难溶化合物，从而减少了强化相θ(CuAl2)、S(Al2CuMg)相的数量，使硬铝的时效强化效果降低，因此镍含量应限制在0.1%以下。锌在硬铝中以杂质存在，它对硬铝的室温力学性能没有影响，但降低硬铝的热硬性，并增加焊接时形成裂纹的倾向，也需严加控制。硬铝合金按其合金元素含量及性能不同，可分为三种类型：即低强度硬铝，如2A01、2A03、2A10等合金；中强度硬铝如2A11 等合金；高强度硬铝，如2A12等合金。1.低强度硬铝这类硬铝合金镁含量较低（2A10）或含铜、镁量都比较低（2A01）。其主要强化相是θ(CuAl2)相，所以时效强化效果较小，强度比较低，具有较高的塑性，而且时效硬化速度比较缓慢。时效强化后具有较高的剪切抗力，适宜作铆接材料。2.中强度硬铝中强度硬铝亦称标准硬铝。这类合金的铜、镁含量都比较高。它在图6-9中（如2A11合金）处于α(Al)+θ(CuAl2)+S(Al2CuMg)相区左侧，主要强化相亦是θ(CuAl2)相，其次是S(Al2CuMg)相。但铜和镁总量较高，镁量较低，因此具有较高的强度和较好的塑性。退火后工艺性能良好，可进行冷弯、冲压等工艺过程焊接性能良好，耐蚀性中等。被切削加工性在退火状态比较差，但时效硬化状态被切削加工性良好。主要用作中等载荷的结构零件。3.高强度硬铝为了提高硬铝合金的强度和屈服极限，在中强度硬铝的基础上，同时提高铜和镁的含量或单独提高镁的含量而形成高强度硬铝。，如2A12合金。它在图6-9中处于α(Al)+θ(CuAl2)+S(Al2CuMg)相区的右侧。其主要强化相是S(Al2CuMg)相，其次是θ(CuAl2)相。由于S相的自然时效强化效果比θ相强，故2A12合金具有比2A11更高的强度和屈服极限以及良好的耐热性，但塑性和某些工艺性能较差些。2A12合金是工业中应用最广泛的一种高强度硬铝合金。硬铝合金的耐蚀性比防锈铝要差的多，特别是在海水中的耐蚀性更差。所以凡需要在腐蚀环境中工作的硬铝合金零件，其表面都要包一层高纯度铝，以提高其抗蚀能力，但是，包铝的硬铝材料热处理后的力学性能要比未包铝的低些。硬铝淬火加热的过烧敏感性很大，为获得最大固溶度的过饱和固溶体，2A12合金最理想的淬火温度为500±3℃，但实际生产条件下很难办到，所以2A12合金常用的淬火温度为495～500℃。硬铝合金淬火加人工时效状态比淬火加自然时效具有更大的晶间腐蚀倾向，所以除高温工作的构件外，一般采用自然时效。2A12合金淬火后自然时效与力学性能的关系。 淬火冷却速度对硬铝合金的强度及耐蚀性都有强烈的影响。当淬火冷却速度低时，由于淬火过程中强化相，如θ(CuAl2)相沿晶界大量析出，而降低自然时效强化效果和增大晶间腐蚀倾向。因此硬铝合金淬火时，在保证不变形开裂的前提下，冷却速度愈快愈好。对于2A11和2A12合金，淬火冷却速度分别不小于20℃/s和14℃/s，通常采用清水作淬火介质。三、超硬铝合金铝-锌-镁-铜系合金是目前室温强度最高的一类铝合金，其强度达500～700 MPa，超过高强度的硬铝2A12合金（400～430 MPa），故称为超硬铝合金。超硬铝合金的牌号及化学成分见表6-2。超硬铝合金中，主要合金元素是锌、镁、铜，有时还加入少量锰、铬、钛等元素。锌和镁是合金的主要强化元素，在合金中形成强化相η（MgZn2）和T(Al2Mg3Zn3)相，它们在铝中都有很大的溶解度变化，具有显著的时效强化效果。但含锌、镁量过高时，虽然合金强度很高，但塑性和抗应力腐蚀性能降低。在合金中加入一定量铜，可以改善超硬铝的抗应力腐蚀性能，同时铜还能形成θ(CuAl2)和S(Al2CuMg)相起补充强化作用，提高合金强度。但铜含量超过3%时，合金的耐蚀性反而降低，故超硬铝合金中的铜含量应控制在3%以下。在超硬铝中加入锰和铬可以提高合金在淬火状态下的强度和人工时效强化效果，同时改善合金的抗应力腐蚀性能。铁和硅都是有害杂质，。铁与锰形成难溶的复杂化合物相，降低合金的力学性能，并使铆接性能变差。硅在合金中夺取镁形成Mg2Si相，使合金中主要强化相η（MgZn2）和T(Al2Mg3Zn2)相的数量减少，降低时效强化效果。铁和硅同时存在时，对超硬铝合金的性能影响比单独存在时要小。如铁和硅的含量均低于0.5%。时，实际上对合金的力学性能没有影响。7A04合金的主要强化相是η相和T相，其次为S相，若在7A04合金的基础上稍提高锌、镁、铜含量，如7A06合金的组织中，η相与T相数量增多，而S相减少，则合金具有更强烈的时效强化效果，故7A06比7A04合金热处理后具有更高的强度，Rm可达600～700 MPa。超硬铝和硬铝比较，淬火温度范围比较宽。对于6%Zn和含3%Mg以下的合金，淬火温度为450～480℃。但淬火温度不宜超过480℃，否则会降低合金的耐蚀性能。合金淬火时应尽量缩短淬火转移时间，以防止含铜相析出，降低合金时效效果。超硬铝热处理与硬铝不同，超硬铝自然时效的时间很长，要经50～60天才能达到最大强化效果；此外自然时效的超硬铝比人工时效的具有更大的应力腐蚀倾向，因此超硬铝均采用人工时效处理。为了进一步提高合金的抗应力腐蚀性能，可采用分级人工时效，即在120℃时效6小时，然后再在160℃时效3小时，以进一步消除内应力。超硬铝若退火后空冷，有淬火效应。因此，退火冷却速度不易过快,一般不大于30℃/h，炉冷至150℃出炉空冷。超硬铝合金的主要缺点是耐蚀性差。为了提高合金的耐蚀性能，一般板材表面包含有1%Zn的包铝层。此外，超硬铝的室温强度虽比硬铝高得多，但耐热强度不如硬铝，当温度升高时，超硬铝合金中固溶体迅速分解，强化相聚集长大，而使得强度急剧降低。故超硬铝合金不宜在120～130℃温度以上工作。超硬铝主要用作受力较大的结构零件。四、锻铝合金铝-镁-硅-铜系合金具有优良的锻造工艺性能，主要用作制造外形复杂的锻件，故称为锻铝合金。锻铝合金的牌号及化学成分见表6-2。锻铝合金是在铝-镁-硅系合金的基础上发展起来的。铝中加入镁和硅能形成Mg2Si化合物，它在铝中有较大的固溶度，且随温度降低而急剧减小。当Mg2Si相从过饱和固溶体中析出时引起晶格严重崎变，故Mg2Si相是一个极有效的强化相。但是，Mg2Si相具有一定的自然时效强化倾向，若淬火后不立即时效处理，则会降低人工时效强化效果。为了弥补这种强度损失，在铝-镁-硅系中同时加入铜和少量锰。在铝-镁-硅-铜系中，锰的主要作用不仅是阻止在结晶退火时晶粒粗大，而且还能提高合金的淬火温度上限，从而提高合金在淬火态的强度。加入铜，可显著地改善热加工塑性和提高热处理强化效果，并且还能抑制挤压效应，降低因加入锰而引起的各向异性。铝-镁-硅-铜系锻铝合金的相组成主要是a、Mg2Si、W(Cu4Mg5Si4Alx)相，当合金中铜含量较高时，亦有θ（CuSi2）和S(Al2CuMg)相。锻铝合金的热处理由于共同的强化相Mg2Si和W(Cu4Mg5Si4Alx)相在室温下析出缓慢，所以在自然时效时很难达到最大的强化效果，必须采用人工时效。锻铝合金热处理的共同缺点是淬火后在室温下的停留时间不宜过长，否则显著降低人工时效强化效果。而且停留时间愈长，人工时效强化效果愈差。因此，锻铝合金淬火后应立即进行时效处理。 铸造铝合金铸造铝合金除要求具备一定的使用性能外，还要求具有优良的铸造工艺性能。成分处于共晶点的合金具有最佳铸造性能，但由于此时合金组织中出现大量硬脆的化合物，使合金的脆性急剧增大。因此，实际使用的铸造合金并非都是共晶合金，它与变形铝合金相比较只是合金元素含量高一些。铸造铝合金的牌号按着GB/T8063-1994标准，用“ZAl＋主加元素符号和百分比含量＋辅加元素符号和百分比含量＋辅加元素符号和百分比含量……”表示。铸造铝合金的代号用“铸造”二字的汉语拼音第一个大写字母“ZL”加三位数字表示。第一位数表示合金系别：1表示为铝硅系合金；2表示为铝铜系合金；3表示为铝镁系合金；4表示为铝锌系合金；如ZL110表示10号铝硅系合铸造铝合金，一、铝-硅铸造合金铝-硅合金具有极好的流动性，铸造收缩性和线膨胀系数小，优良的焊接性、耐蚀性以及足够的力学性能。但合金的致密度较小，适宜制造致密度要求不太高的、形状复杂的铸件。在简单的二元铝-硅合金中，加入某些强化元素后组成的多元铝-硅合金称为特殊铝-硅合金。1.简单的铝-硅合金简单的二元铝-硅合金（ZL102）是硅含量11%～13%的合金。铸造后的组织为粗大的针状硅与铝基固溶体组成的共晶体和少量的板块状初晶硅。由于组织中粗大的针状共晶硅的存在，合金的力学性能不高，抗拉强度Rm不超过140 MPa，延伸率A不小于3%。若浇注前在熔融合金中加入2%～3%的变质剂，进行变质处理，则可以细化组织。常用的变质剂为2/3NaF+1/3 NaCl或25% NaF+62.5%NaCl+12%KCl混合物，经搅拌均匀后浇入铸型。经变质处理后的ZL02合金的抗拉强度Rm达180MPa，延伸率A可达8%。铝-硅合金变质处理虽能细化组织，改善力学性能，但由于变质剂钠易与熔融合金中的气体起反应，使变质处理后的铝合金铸件产生气孔（亦称针孔）等铸造缺陷，为了消除这种铸造缺陷，浇注前必须进行精炼脱气，致使铸造工艺复杂化。故目前对于硅含量小于7%～8%的合金一般都不进行变质处理。简单的铝-硅合金经变质处理后，可以提高力学性能。但由于硅在铝中的固溶度变化不大，且硅在铝中的扩散速度很快，极易从固溶体中析出，并聚集长大，时效处理时不能起强化作用，故简单铝-硅合金的强度不高。为了进一步提高铝-硅合金的力学性能，常加入铜、镁等合金元素，形成时效强化相，并通过热处理强化，进一步提高力学性能，以扩大其应用范围。2.含镁特殊铝-硅合金若在铝-硅合金中加入适量的镁，能形成Mg2Si相，它在α固溶体中的固溶度随温度降低而显著减小。在固溶处理时能全部溶入α固溶体，经时效处理能产生显著的强化效果。但镁的加入量过高时，固溶处理后尚有一部分未溶解的过剩相Mg2Si存在，使合金变脆。常用的特殊铝-硅合金有ZLl04、ZLl01等合金。例如，ZL104合金的成份标于图中所示位置，在室温时的平衡组织为α固溶体与(α+ Si)二元共晶体以及自α固溶体中析出的Mg2Si相。热处理后的抗拉强度Rm达240 MPa，延伸率为3.6%。铸造、焊接、耐蚀性能等均较高。3.含铜特殊铝-硅合金在铝-硅合金中加入铜能形成θ (CuAl2)强化相，通过热处理能进一步提高合金强度。常用的含铜特殊铝-硅合金有ZL107合金， ZL107经热处理后抗拉强度达260MP，延伸率为3%。4.含铜、镁特殊铝-硅合金铝-硅合金中同时加铜、镁形成的多元合金。．其组织中除Mg2Si、CuAl2等相外，还有Al2CuMg、W（AlxCu4Mg5Si）等强化相。常用的合金有ZL103、ZL105、ZL110等合金。多元特殊铝-硅合金，因其热处理后具有更高的力学性能，故可用作受力较大的内燃机零件，如缸体、缸盖、曲轴箱等。二、铝-铜铸造合金铝-铜铸造合金的最大特点是耐热性高，是所有铸造铝合金中最高的一类合金。其高温强度随铜含量的增加而提高，而合金的收缩率和形成裂纹的倾向则减小。但由于铜含量增加，使合金的脆性增加，故铸造铝台金的铜含量一般不超过14%。铝-铜合金的最大缺点是耐蚀性差，且随铜含量的增加耐蚀性降低。铜含量不同，铝-铜铸造合金的性能特点不同，其用途并不一样。铜含量4%～5%的合金热处理强化效果最好，具有高的强度和塑性，但铸造性能较差。例如ZL203合金适宜制造形状比较简单强度要求较高的铸件。中等铜含量(8%～10%左右）的合金热处理强化效果较差，但铸造性能较好，例如ZL202合金适宜铸造形状复杂，但强度和塑性要求不太高的大型铸件。铜含量高的合金具有高的耐热性能和优良的铸造性能。适宜铸造形状复杂和在高温工作的铸件，如汽车、摩托车发动机的活塞等。三、铝-镁铸造合金铝-镁铸造合金是密度最小（2.55)、耐蚀性最好、强度最高（抗拉强度可达350MP)的铸造铝合金。但由于结晶温度范围宽，故流动性差，形成疏松倾向大，其铸造性能不如铝-硅合金好，且熔化浇铸过程中易形成氧化夹渣，使铸造工艺复杂化。此外，由于合金的熔点较低，故热强度较低，工作温度不超过200℃。常用的铝-镁铸造合金有ZL301、ZL302合金。ZL301合金由α固溶体及其析出的Mg5Al8相所组成。由于铝-镁合金时效处理过程中不经历GP区阶段，而直接析出Mg5Al8相，故时效强化效果较差，且强烈降低合金的耐蚀性和塑性。因此ZL301合金常以淬火状态使用。ZL301合金经固溶处理后抗拉强度Rm达350MPa，延伸率达10%。铝-镁铸造合金常用做制造承受冲击、振动载荷和耐海水或大气腐蚀、外形较简单的重要零件和接头等。四、铝-锌铸造合金锌在铝中的溶解度很大，极限溶解度为32%。铝中加入10%以上的锌能显著提高合金的强度，故铝锌铸造合金具有较高的强度，是最便宜的一种铸造铝合金，其主要缺点是耐蚀性差。常用的铝-锌铸造合金是ZL401合金。由于这种合金含有较高(6.0%～8.0%）的硅，又称含锌特殊铝-硅合金。在合金中加入适量的锰、铁和镁，可以显著提高合金的耐热性能。主要用于制作工作温度不超过200℃，结构形状复杂的汽车、飞机零件、医疗机械和仪器零件等。五、铸造铝合金的热处理特点及代号铸造铝合金中除了铝-硅合金ZL102、铝-镁合金ZL302外，所有其他合金均能热处理强化。铸造铝合金与变形铝合金比较，其组织粗大，有严重的晶内偏析和粗大的针状化合物。此外，铸件的形状亦比较复杂。因此，铸造铝合金的热处理除了具有一般变形铝合金的热处理特性外，淬火加热温度一般比较高，保温时间比较长，一般均在15～20小时左右。其次，由于铸件的形状比较复杂，壁厚不均匀，为了防止淬火时引起变形开裂，一般采用温度较高（60～100℃）的水作淬火冷却介质。此外，为了保证铸件的耐蚀性以及组织与性能和尺寸稳定性，凡是需要时效处理的铸件，一般都采用人工时效。铸造铝合金的热处理可根据铸件的工作条件和性能要求，选择不同的热处理方法。能力知识点6 耐热铝合金一、耐热铝合金的合金化耐热铝合金的合金化与耐热钢相类似，主要也是通过固溶强化、过剩相强化和晶界强化等几方面来提高其热强性的。1.固溶强化耐热铝合金的固溶强化，要求加入的合金元素与形成的固溶体具有高的热强性，而不显著降低合金的熔点，以保证合金具有较高的再结晶温度。其次，加入的合金元素要能增大原子间的结合力，减慢原子的扩散过程和固溶体分解速度。耐热铝合金通常采用多种合金元素进行合金化。这些合金元素加入后一般降低合金的熔点很少。它们多数是一些熔点比铝高的过渡族元素，常用的合金元素有锰、铁，铜、锂以及稀士元素等。2.过剩相强化耐热铝合金大多是多相合金，一定数量的耐热性能好的过剩相是耐热铝合金不可缺少的，熔点高的、成分和结构复杂、并在高温下与共存的固溶体互相作用微弱的过剩相，具有高的热稳定性。铝合金中热稳定性好的过剩相有A12CuMg(S)、AI6Cu3Ni(T),、Al.xCu,4Mg5Si4(W)、AI2FeSi等。3.晶界强化在铝合金中加入钛、锆和稀土元素等都能有效地强化晶界。特别是稀土元素能与铝中的多种杂质元素起作用，清除晶界处的杂质、达到净化晶界与提高晶界抗蠕变的目的，从而显著地提高铝合金的耐热性能。二、耐热铝合金牌号耐热铝合金根据加工工艺特点不同可分为耐热变形铝合金和耐热铸造铝合金。常用耐热变形铝合金牌号有：2A02、2A16、2A17、2A70、2A80、2A90等；常用耐热铸造铝合金牌号有：ZL110、ZL108、ZL109等，1.耐热变形铝合金1）．耐热硬铝合金耐热硬铝合金为铝-铜-锰系合金，常用的有2A02、2A16、2A17合金。铜和锰是这类合金的重要组成元素。铜含量为6.0%～6.5%的合金具有高的再结晶温度，因此耐热性能高；同时铜的加入能形成CuAl2强化相，通过人工时效可使合金强化。锰在铝中的扩散系数小，并降低铜在铝中的扩散速度，减慢α固溶体的分解和减小强化相在高温下聚集长大倾向，是保证合金耐热性的主要元素。合金的锰含量在0.4%～0.5%时，能形成细小弥散的T (CuMn2Al12）相，提高合金的耐热性。但锰含量超过1.2%时，由于T相数量增多，相界面增加，加速了扩散过程，使合金耐热性降低。因此，在耐热硬铝合金的锰含量应控制在0.4%～0.8%。合金中加入少量钛能细化组织且提高合金的再结晶温度，因而提高合金的耐热性。但钛含量超过0.2%时，反而使合金耐热性降低，故钛含量应控制在0.1%～0 .2%。2A17合金是在2A16 的基础上加入0.25%～0.45% Mg的合金。镁能提高合金的室温强度，有利于提高合金在150～250℃下的耐热性能，但它使合金的焊接性能变坏，故应控制在0.5%以下。耐热硬铝主要用于制作挤压和模锻的半制品，制造在200～300℃下工作的零件，如压缩机叶片盘或加工成板材用作常温和高温下工作的焊接容器。2）.耐热锻铝合金耐热锻铝合金属于铝-铜-镁-铁-镍系合金，铝-铜-镁-铁-镍系合金属于耐热锻铝合金，常用的牌号是2A70,2A80、2A90合金。这类合金中的主要耐热相为S(A12CuMg)相，因此，合金中应力求使S(A12CuMg)相的数置达到极限值。为此，合金中应相对地降低铜含量，而适当提高镁含量，以保证获得最大数量的S(A12CuMg)相，从而获得优良的耐热性能。铁和镍按1:1的比例同时加入合金时，能形成FeNiAl9，对提高合金的耐热性有良好的作用。但合金中单独加入铁或镍时，都使合金的耐热性降低。耐热锻铝合金除了具有较好的耐热性外，还具有小的热膨胀系数，良好的导热性以及加工工艺性能。可加工成各种棒材、锻件以及制作在150～225℃下工作的结构零件。2.耐热铸造铝合金活塞是发动机中传递能量的一个重要零件，它在工作时承受高温、高压、并高速地往复运动。因此，作为活塞材料，除了要求密度小、导热性好外，还要求具备优良的耐热性和耐磨性以及良好的加工工艺性。活塞铝合金是典型的耐热铸造铝合金。它是在二元铝-硅合金ZL102的基础上，分别加入一定量的铜、镁、镍、锰及稀土元素等，组成的多元铝-硅铸造合金。其中铝-硅-铜-镁系的ZL110和ZL108以及铝-硅-铜-镁-镍系的ZL109合金，是最常用的耐热铸造铝合金，主要用于制造活塞。铝-硅合金中加入铜和镁能形成CuAI2和Mg2Si以及W(AI5Mg5Cu4Si4）相，起强化作用，但镁量过高会出现粗大的过剩相Mg2Si，使合金变脆，并使合金的吸气性增加。锰能提高合金的耐热性。它在固溶体中的扩散系数很小，当合金凝固时锰被保留在固溶体中，起固溶强化作用，提高了固溶体在高温下的稳定性，从而提高合金的耐热性。锰还能形成具有高温硬度的T(CuMn2Al12)相，显著提高合金的热硬性。镍在合金中能形成具有热硬性的AI3Ni或〔CuNi）2AI3相，提高合金的热强度。在ZL109合金组织中主是α, Si, Mg2Si, AI3Ni等相。耐热铝合金的热处理必须保证在工作温度下具有高的组织与性能稳定性。因此，耐热铝合金固溶处理后，均采用人工时效处理。