化工毕业论文百度云

固体氧化铁脱硫剂长期以来因硫容量低,用于高含硫气体时,存在着在高空速下气体净化度不高的问题,限制了氧化铁脱硫剂的应用。因此本文综合目前应用最为广泛氧化铁脱硫剂的优缺点，分别探讨不同反应物制得的Fe2O3脱硫剂的脱硫性能及不同载体在不同温度下的脱硫效果，且在这些条件下再改变沉淀剂的种类来深入探讨出一种高效的、成本较低的脱硫剂。Solid oxide sulfur sorbent capacity due to low long-term, for high-sulfur gas, the existence of the gas at high speed is not high degree of purification of the problem, limiting the application of iron oxide sorbent. Therefore this paper, the current most widely used iron oxide desulfurizer the advantages and disadvantages of different reactants were obtained desulfurizer Fe2O3 and the desulfurization performance of different carriers at different temperatures desulfurization effect, and under these conditions in the precipitation agent to change the type of depth to a highly efficient, lower-cost sorbent.首先，通过选择不同的反应原料来制取脱硫剂，即分别使用实验室的Fe2O3原料、FeCl3和Fe2(SO4)3来制备脱硫剂。结果发现经过酸化后的Fe2O3原料所制取的脱硫剂脱硫性能较好。其主要原因是其他两种原料在反应后抽虑过程中有Cl-、SO42-未完全洗涤掉，进而对脱硫剂脱硫效果产生了影响。First of all, by selecting the different reactions to the preparation of raw materials desulfurizer, that the use of raw materials Fe2O3 Laboratory, FeCl3 and Fe2 (SO4) 3 to prepare desulfurizer. The results showed that after acidification of the raw material after the preparation of Fe2O3 Desulfurization of better performance. The main reason is the other two after the extraction of raw materials in the reaction process to consider Cl-, SO42-has not been completely washed out, and thus the effect Desulfurization impact.其次，选择Fe2(SO4)3为原料制取脱硫剂，当温度一定，改变载体的种类，发现相同温度下Al2O3为载体的效果最佳，载体C效果最差，其一方面的原因是载体C焙烧后脱硫剂的强度很差，基本成粉末状。而Al2O3的最好。与此同时，当固定一种载体时，通过改变焙烧温度来考察脱硫剂性能。结果表明，脱硫剂的最佳焙烧温度为450℃。Secondly, the choice of Fe2 (SO4) 3 as raw materials desulfurizer preparation, when the temperature must change the type of carrier and found the same temperature as the carrier under the effect of Al2O3 best, the worst effects of carrier C, which was due to carriers on the one hand, C After calcination the intensity of desulfurizer poor basic into powder. The best and Al2O3. At the same time, when a carrier of fixed by changing the calcination temperature to study the performance desulfurizer. The results showed that the best sorbent calcination temperature to 450 ℃.再次，当选用沉淀剂NH4OH、NH4HCO3、Na2CO3，发现沉淀剂的效果是NH4OH＞NH4HCO3＞Na2CO3。另外，当固定载体种类时，改变载体CaO的含量（10％、20％、30％），发现载体的含量越低时脱硫效果越好。将上述所有脱硫剂经过900℃焙烧2小时进行老化，再次进行脱硫反应，结果发现，老化后的脱硫效果远远比未被老化的脱硫剂效果差。Re-elected with precipitant NH4OH, NH4HCO3, Na2CO3, found that the effect of precipitant NH4OH> NH4HCO3> Na2CO3. In addition, the type of when a fixed vector, the change in CaO content vector (10%, 20%, 30%) and found that the lower carrier concentration, the better when the desulfurization effect. Desulfurizer above all after two hours baking 900 ℃ for aging of desulfurization again found that the effect of aging is much lower than those of the desulfurization aging desulfurizer not bad.最后，通过改变H2S空速、是否含有水蒸气来讨论对脱硫效果的影响，研究表明，随着空速的增大，脱硫剂的脱硫性能降低，而H2S中不含有水蒸气能产生较好的脱硫效果。 Finally, by changing the space velocity H2S, to discuss whether it contains water vapor effect on the desulfurization, research showed that with increasing airspeed, the desulfurization sorbent performance, and H2S does not contain water vapor to produce better desulfurization.

化工类毕业论文范文辉光放电在减压反应器中进行，在直流、低频交流、射频，或者微波电场或磁场的作用下产生。反应装置有内极式、外极式和无极感应式等3种。低温等离子体化学反应的优点在于：在常规下不能进行或难以进行的反应，在等离子体状态下能够顺利进行，如全氟苯的聚合、氮化硅的淀积等。等离子体表面轰击力强，穿透力弱，适合于表面改性。等离子体表面改性时，主要是利用各种能量粒子与固体表面作用，达到改变表面化学结构的目的。它包括3方面内容： 在A r、He、N2、O2和NH3等气体的辉光放电中对聚合物表面进行等离子体处理;进行等离子体接枝;在聚合物表面淀积超薄等离子体聚合膜。与常规化学改性方法相比，等离子法具有干法、不破坏材质、低温、快速、污染小和效率高等优点。 低温等离子体的特点 低温等离子体含有大量的电子、激发态原子和分子以及自由基等活性粒子,这些活性粒子使材料表面引起蚀刻、氧化、还原、袭解、交联和聚合等物理和化学反应,对材料表面进行改性。由于低温等离子体中粒子的能量一般为几个至几十个电子伏特,大于高分子材料的结合键能(几个至十几个电子伏特),完全可以使有机大分子材料的结合键断裂而形成新键;但其健能远低于高能放射线的能量,故表面等离子体处理只发生在材料的表面,在不损伤基体的前提下,赋予材料表面新的性能。 低温等离子体在高分子材料上的应用，大致可以分为两类：一是等离子体聚合，另一是等离子体改性。等离子体聚合是利用聚合性气体，在基底表面生成具有特殊功能(如防水、防腐蚀、结构致密具有特殊物理性能等)的聚合物;等离子体改性是利用各种等离子体系作用于物质表面，在物质表面发生各种物理和化学的作用，如架桥、降解、交联、刻蚀、极性基团的引入及接枝共聚等，从而达到对物质表面改性的目的。用高分子膜作为等离子体聚合物的沉积基质会引起材料表面的交联、化学物理性质以及形态的改变，从而起到了对原高分子膜改性的作用。 机理分析 等离子体处理橡胶表面是利用气体(空气或氧气)电离产生氧等离子体，氧等离子体中大量的 O+、O-、O+2、O-2、O、O3、臭氧离子、亚稳态 O2 和自由电子等粒子与橡胶表面发生物理和化学反应，在橡胶表面产生大量的极性基团，使碳原于从C—H结合变为 、 、 等，从而提高橡胶表面的亲水性，改善橡胶与金属的粘合性能。 等离子体粒子的能量一般约为几个到几十个电子伏特，如电子的能量为0—20eV，离子为0—2eV，亚稳态粒子为0—20eV，紫外光/可见光为3—40eV。而橡胶中常见化学键的键能为：C—H ;C=0 ;C—C ;C=C 。由此可见，等离子体中绝大部分粒子的能量均略高于这些化学键能，这表明等离子体是完全有足够的能量引起橡胶内的各种化学键发生断裂或重新组合的。以聚丁二 烯 橡胶为例来说明： 尽管反应仅在表面几个单分子层发生(只限于橡胶表面最外层10—1000的范围内，不会改变橡胶的整体特性)，但是其密度和强度的增加却说明表面能的改变。 低温等离子体处理的过程 对聚合物的低温等离子体处理包括以下4个过程:脱离(Ablaton);交联(Cross-linking);活化(Activation)和沉积(Deposition)。 (1)脱离：等离子体处理过程中,利用高能粒子轰击聚合物,使弱的共价键断裂,称为脱离。脱离使得暴露在等离子体中基质的最外分子层离开基体,由真空装置除去。由于基质表面污染层的化学键一般由较弱的C-H键构成,故等离子体处理可以除去像油薄膜一样的污染物,使基质表面清洁,并留下活性的聚合物表面。